• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Mémoire de Maîtrise
DOI
10.11606/D.46.2007.tde-21052007-195731
Document
Auteur
Nom complet
Daniela Manz
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2007
Directeur
Jury
Kawano, Yoshio (Président)
Catalani, Luiz Henrique
Wiebeck, Hélio
Titre en portugais
Caracterização vibracional e térmica de filmes poliméricos utilizados como substrato em curativos adesivos
Mots-clés en portugais
Caracterização de materiais
Curativos adesivos
Filme polimérico
Módulo de elasticidade
Permeabilidade ao vapor d'água
Polímeros
Resumé en portugais
Um filme polimérico utilizado na fabricação de curativos adesivos não perfurados deve ter baixo módulo de elasticidade e boa permeabilidade ao vapor d' água. O baixo módulo de elasticidade garante sensação de maior conforto do produto em contato com a pele quando a pessoa que o está utilizando movimenta a parte do corpo sobre a qual está aplicado o curativo, principalmente a região das articulações, como joelhos e cotovelos. A importância de uma boa permeabilidade ao vapor d' água está relacionada, principalmente em curativos não perfurados, ao fato de que a pele perde água constantemente e, se o filme polimérico não permitir a saída dessa água ao meio ambiente, ocorrerá um fenômeno denominado maceração, que é a sensibilização excessiva da pele, causada pela hiper hidratação da mesma. O presente trabalho apresenta um estudo da permeabilidade ao vapor d' água, bem como a caracterização vibracional e térmica de um filme polimérico constituído por três polímeros diferentes, desenvolvido para substituir a poliuretana utilizada atualmente na produção de curativos adesivos não perfurados, com custo inferior. Os polímeros que constituem o filme foram caracterizados separadamente e alguns resultados obtidos, como Tm e a estrutura química dos polímeros Lotader® e Lotryl® foram comparados aos dados fornecidos pelo fabricante. Verificou-se que as propriedades de módulo de elasticidade e permeabilidade ao vapor d' água do filme desenvolvido são inferiores às da poliuretana inviabilizando a substituição. Entretanto, o trabalho proporcionou um melhor entendimento dos fatores que influenciam o módulo de elasticidade e a permeabilidade do novo material ao vapor d' água.
Titre en anglais
Vibrational and thermal characterization of polymeric films used as substrate in adhesive tapes
Mots-clés en anglais
Adhesive tapes
Elasticity modulus
Materials characterization
Polymer
Polymeric film
Vapor water permeability
Resumé en anglais
A polymeric film must have low elasticity modulus and good water vapor permeation to be used in the production of non perforated adhesive tapes. Low modulus is desirable to provide comfort sensation as the consumer moves the part of his or her body in which the tape is applied on, mainly in the articulations regions, as elbows and knees. The importance of good water vapor permeation is related, mainly in the case of non perforated adhesive tapes with the continuous loss of water by the skin. If the film does not allow the release of the water continuously lost by the skin to the environment, the skin will become very sensitiveness as a result of over hydration. This work presents a study of water permeability and a thermal and vibrational characterization of a polymeric film composed of three different polymers developed to replace the adhesive not perforated polyurethane tape providing lower cost. Besides characterization a test of Water Vapor Transmission Rate (WVTR) was performed. Each polymer present in the film composition was analyzed and the results as Tm and chemical structure of Lotader® e Lotryl® were compared with the producer data. It was verified that the properties of elasticity modulus and water vapor permeability of the new material developed are worse than polyurethane so the substitution can not be performed. However, the work provided a better understanding of the factors that influences the elasticity modulus and water vapor permeability of the new material.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
dissertacaomanz.pdf (3.54 Mbytes)
pretexto.pdf (165.68 Kbytes)
signifie que le fichier ne peut être consulté à l'intérieur du Unversité de São Paulo.
Date de Publication
2007-07-04
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.