Dissertação de Mestrado
DOI
10.11606/D.97.2010.tde-26092012-140655
Documento
Autor
Nome completo
André Brauner
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Lorena, 2010
Orientador
Banca examinadora
Machado, Antonio Jefferson da Silva (Presidente)
Jardim, Renato de Figueiredo
Oliveira Junior, Nei Fernandes de
Título em português
Estudo das propriedades supercondutoras da fase T2 no sistema Nb-Si-B
Palavras-chave em português
Estrutura lamelar
Fase T2 no sistema Nb-Si-B
Intersticial
Supercondutividade
Resumo em português
Este trabalho tem como objetivo o estudo da influência do boro na fase αNb5Si3 (Fase T2) a baixas temperaturas analisando suas propriedades elétricas e magnéticas. Para o estudo deste tema as amostras foram preparadas, seguindo a estequiometria Nb5Si3-xBx, via metalurgia do pó e também por fusão a arco, com x dentro do intervalo limitado por 0  X  1,0. Estas amostras foram analisadas através de difratometria de raios x, microscopia eletrônica de varredura, magnetização, transporte elétrico e medidas calorimétricas em baixa temperatura. As medidas das propriedades elétricas e magnéticas destas fases mostram que a substituição de boro por silício induz supercondutividade na fase T2. O caráter volumétrico da transição supercondutora é confirmado pela medida de capacidade calorífica. Assim, este trabalho é o primeiro a mostrar uma nova família de materiais supercondutores que cristalizam na estrutura protótipo Cr5B3.
Título em inglês
Study of superconducting properties of the T2 phase in the system Nb-Si-B.
Palavras-chave em inglês
interstitial and T2 phase in the system Nb-Si-B
Lamellar structure
new superconducting material
Superconductivity
Resumo em inglês
This work to study the influence of boron during low temperature αNb5Si3 (T2 phase) analyzing their electrical and magnetic properties. For the study of this subject the samples were prepared, following the stoichiometry Nb5Si3-xBx via powder metallurgy and also by arc melting process, with x within the range limited by 0X1.0. These samples were analyzed by X-ray diffraction, scanning electron microscopy, magnetization, electrical transport and calorimetric measurements of low temperature. Measurements of electrical and magnetic properties of these phases show that the substitution of boron by silicon induces superconductivity at the T2 phase. The bulk nature of superconducting transition is confirmed by heat capacity measurement. This study is the first to show a new family of superconducting materials that crystallize in the Cr5B3 prototype structure.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
EMD10005.pdf (1.15 Mbytes)
Data de Publicação
2012-09-26
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.