Master's Dissertation
DOI
https://doi.org/10.11606/D.85.2017.tde-23052017-152804
Document
Author
Full name
Bruno Pizol Invernizzi
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2017
Supervisor
Committee
Neves, Maurício David Martins das (President)
Berretta, José Roberto
Couto, Antonio Augusto
Title in Portuguese
Soldagem circunferencial do aço inoxidável super duplex UNS S32750 pelo processo MIG com controle CMT®
Keywords in Portuguese
aço inoxidável super duplex
caracterização microestrutural
ensaio de corrosão
propriedades mecânicas
soldagem MIG com controle CMT
Abstract in Portuguese
Neste trabalho foram realizados experimentos de soldagem circunferencial em tubos de aço inoxidável super duplex UNS S32750, com diâmetros de 19,05 mm e 48,20 mm. Foram executadas soldas utilizando-se diversos parâmetros de soldagem num equipamento MIG com controle CMT® Cold Metal Transfer. Os cordões de solda foram avaliados por inspeção visual e dimensional, além dos ensaios de tração e microdureza Vickers, bem como a análise microestrutural em conjunto com análise de precipitação de fases, a qual foi realizada em acordo com a prática A da norma ASTM A923, e ensaio de corrosão conforme a prática A da norma ASTM G48 em conjunto com a norma ASTM A923. Os resultados indicaram que a soldagem do tubo com diâmetro de 19,05 mm apresentou cordão de solda com dimensões inaceitáveis conforme norma, tendo sido esta condição atribuída a utilização de um elevado diâmetro do arame para as condições (parâmetros) usadas de soldagem. A soldagem do tubo com diâmetro de 48,20 mm apresentou falta de penetração nas condições empregadas, quando soldado pelo processo CMT® convencional. No caso da utilização do CMT® combinado com arco pulsado, em condições que geraram maior aporte de calor durante a soldagem, assim obteve-se penetração total da junta e acabamento superficial adequado. Os resultados indicaram que a soldagem utilizando o processo CMT® combinado com arco pulsado, nas condições (parâmetros) empregados geraram bom acabamento superficial, aliado propriedades mecânicas compatíveis, atendendo exigências de normas, bem como uma microestrutura balanceada e alta resistência à corrosão.
Title in English
Circunferencial welding aplied for inox steel super duplex UNS S32750 using the process MIG using CMT® control
Keywords in English
corrosion tests
mechanical properties
metallographic examination
MIG-welding CMT
stainless steel super duplex
Abstract in English
This study carried out circumferential welding experiments in UNS S32750 Super Duplex Stainless Steel tubes using diameters of 19,05 mm and 48,20 mm. Welds were performed using various welding parameters on a MIG machine with Cold Metal Transfer® CMT control. The weld joints were evaluated by visual and dimensional inspection in addition to the Vickers microhardness and traction tests, as well as the microstructural analysis in conjunction with phase precipitation analysis, which was performed according to practice A of ASTM A923, and corrosion test in accordance with practice A of ASTM G48 in conjunction with ASTM A923. The results indicated that welds performed in pipes with a diameter of 19.05 mm showed a weld joint with unacceptable dimensions according to the standard, this condition being attributed the use of a high wire diameter for the welding conditions used. Welding performed for pipes with a diameter of 48.20 mm showed a lack of penetration under the conditions employed when welded by the conventional CMT® process. In the case of the use of CMT® combined with pulsed arc, under conditions that generated greater heat input during welding, this resulted in total penetration of the joint and adequate surface finish. The results indicated that welding using the CMT® process combined with pulsed arc, under the conditions (parameters) employed generated good surface finish, combined mechanical properties, meeting standards requirements, as well as a balanced microstructure and high resistance to corrosion.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2017-07-13
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.