Tese de Doutorado
DOI
10.11606/T.85.2006.tde-14052007-150153
Documento
Autor
Nome completo
Sergio Luiz de Assis
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2006
Orientador
Banca examinadora
Costa, Isolda (Presidente)
Freire, Celia Marina de Alvarenga
Higa, Olga Zazuco
Melo, Hercilio Gomes de
Wolynec, Stephan
Título em português
Investigação da resistência à corrosão da liga Ti-13Nb-13Zr por meio de técnicas eletroquímicas e de análise de superfície
Palavras-chave em português
Biomateriais
Corrosão de materiais
Eletroquímica
Ensaio de materiais
Ligas metálicas
Resumo em português
Neste trabalho, a resistência à corrosão in vitro da liga de titânio Ti-13Nb-13Zr, fabricada em laboratório nacional, e destinada a aplicações ortopédicas, foi investigada em soluções que simulam os fluidos corpóreos. Os eletrólitos usados foram solução 0,9 % (massa) de NaCl, solução de Hanks, meio de cultura (MEM), neste dois últimos meios, sem e com adição de peróxido de hidrogênio. A adição de peróxido visou simular condições existentes em caso de processos inflamatórios resultantes de procedimentos cirúrgicos. A resistência à corrosão de ligas já comercialmente consagradas para uso como biomateriais, Ti-6Al-7Nb e Ti-6Al-4V, bem como do titânio puro (Ti-cp), foi também estudada por razões de comparação com a liga Ti-13Nb-13Zr. Foram utilizadas técnicas eletroquímicas e de análise de superfície. As técnicas eletroquímicas consistiram de: (a) medidas da variação do potencial a circuito aberto em função do tempo, (b) polarização potenciodinâmica e (c) espectroscopia de impedância eletroquímica (EIE). Os diagramas experimentais de impedância foram interpretados utilizando circuitos elétricos equivalentes que simulam modelos de filme óxido de estrutura dupla composta de uma camada interna compacta, tipo barreira, e uma camada porosa mais externa. Os resultados mostraram que a resistência à corrosão deve-se principalmente à camada barreira, e indicaram alta resistência à corrosão de todas as ligas e do Ti-cp em todos os meios estudados. O óxido formado na superfície da liga Ti-13Nb-13Zr, seja naturalmente ou em meios fisiológicos, foi caracterizado utilizando espectroscopia de fotoelétrons excitados por raios-X (XPS) e microscopia eletrônica de varredura (MEV). Os resultados mostraram que a presença de peróxido de hidrogênio em MEM promove o crescimento da camada porosa e incorporação de íons minerais, além de favorecer a formação de hidroxiapatita. A citotoxicidade da liga Ti-13Nb-13Zr foi também avaliada e esta se mostrou ser não tóxica.
Título em inglês
Investigation on the corrosion resistance of Ti-13Nb-13Zr alloy by electrochemical techniques and surface analysis
Palavras-chave em inglês
Biomaterials
Corrosion of materials
Electrochemistry
Materials testing
Metallic alloys
Resumo em inglês
In this work, the in vitro corrosion resistance of the Ti-13Nb-13Zr alloy, manufactured at a national laboratory, and used for orthopedic applications, has been investigated in solutions that simulate the body fluids. The electrolytes used were 0.9 % (mass) NaCl, Hanks' solution, a culture medium (MEM), and the two last electrolytes, without and with addition of hydrogen peroxide. The aim of peroxide addition was to simulate the conditions found when inflammatory reactions occur due to surgical procedures. The corrosion resistance of alloys commercially in use as biomaterials, Ti-6Al-7Nb and Ti-6Al-4V, as well as of the pure titanium (Ti-cp), was also studied for comparison with the Ti-13Nb-13Zr alloy. The corrosion resistance characterization was carried out by electrochemical and surface analysis techniques. The electrochemical tests used were: (a) open circuit potential measurements as a function of time, (b) potentiodynamic polarization and (c) electrochemical impedance spectroscopy (EIE). The impedance experimental diagrams were interpreted using equivalent electric circuits that simulate an oxide film with a duplex structure composed of an internal and compact, barrier type layer, and an external porous layer. The results showed that the corrosion resistance is due mainly to the barrier type layer. The titanium alloys and the Ti-cp showed high corrosion resistance in all electrolytes used. The oxides formed on the Ti-13Nb-13Zr, either naturally or during immersion in MEM or Hanks’ solution was characterized by X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (MEV). The results showed that the presence of hydrogen peroxide in MEM promotes the growth of the porous layer and incorporation of mineral ions, besides favouring hydroxyapatite formation. The citotoxicity of the Ti-13Nb-13Zr alloy was also evaluated and it was shown to be non-toxic.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2007-06-22
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.