• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Dissertação de Mestrado
DOI
10.11606/D.76.2003.tde-14012009-113150
Documento
Autor
Nome completo
Ubaldo Martins das Neves
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2003
Orientador
Banca examinadora
Giacometti, José Alberto (Presidente)
Araújo, Eudes Borges de
Nunes, Luiz Antonio de Oliveira
Título em português
Estudo das propriedades de armazenamento óptico e grades de relevo em poliuretano derivado de azo-benzeno
Palavras-chave em português
Armazenamento óptico de informação
Azo-polímero
Birrefringência foto-induzida
Grades de relevo em superfície polimérica
Resumo em português
Polímeros contendo grupos azo-benzênicos têm sido estudados devido a sua capacidade para óptica não linear, formação de superfícies de relevo e de birrefringência fotoinduzida. O fator que possibilita essas aplicações é a propriedade de fotoisomerização reversível trans-cis-trans do grupo azo que produz a sua reorientação molecular. Neste trabalho foram produzidos filmes casting do poliuretano MDI-DR19 derivado de azo-benzeno. Estudou-se o crescimento e decaimento da birrefringência para diferentes valores de potência da luz de excitação da fotoisomerização. Os resultados experimentais do crescimento e decaimento foram analisados usando duas exponenciais e eles mostraram que o polímero MDI-DR19 apresenta boas características para utilização em armazenamento óptico pois cerca de 65% da birrefringência induzida no material permanece por longos intervalos de tempo. Ilustramos o processo de armazenamento de informação gravando uma imagem de birrefringência num filme de MDI-DR19. Foram também produzidas grades de relevo em filmes de MDI-DR19 utilizando franjas de interferência produzidas com luz de polarização P e S. Essas grades apresentaram alta uniformidade e características compatíveis com as mostradas na literatura.
Título em inglês
Information optically storage and relief gratings study in material derivative of azo-benzene polyrethane
Palavras-chave em inglês
Azopolymer
Optical storage of information
Optically induced birefringence
Relief gratings in polymer surfaces
Resumo em inglês
Polymers containing azobenzenic groups have been studied due to their applications on non-linear optics, surface relief gratings (SRG) and photoinduced anisotropy for optical storage. The reversal photoisomerization trans-cis-trans property of the azo group induces a molecular reorientation. In this work, cast films of na azobenzene derivative, the polyurethane MDI-DR19, were studied. The build-up and decay of the birefringence were studied as a function of the photoisomerization exciting light power. The data of the build-up and decay of the birefringence were fitted with a bi-exponential function, which shows the stability of the MDI-DR19 for application in optical storage, since 65% of the induced birefringence remains after a long time. The optical storage is illustrated by recording a birefringence image in a film of MDI-DR19. It was also performed a SRG over films of MDI-DR19 applying an interference finger pattern with a P and S polarized light. The light induced gratings shows good uniformity and characteristics compatible with those presented in the literature.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
UbaldoMartinsNevesM.pdf (783.99 Kbytes)
Data de Publicação
2009-01-19
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.