Tese de Doutorado
DOI
10.11606/T.3.2008.tde-11052009-174233
Documento
Autor
Nome completo
Carlos Eddy Valdéz Salazar
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2008
Orientador
Banca examinadora
Padovese, Linilson Rodrigues (Presidente)
Capó Sánchez, Julio Antonio
Delijaicov, Sergio
Hioki, Daniel
Stipkovic Filho, Marco
Título em português
Avaliação através da inspeção magnética da condição superficial de anéis de rolamento de aço DIN 100Cr6 após torneamento duro a seco.
Palavras-chave em português
Ensaios magnéticos não destrutivos
Processos de fabricação
Ruído magnético de Barkhausen
Tensão residual
Resumo em português
O presente trabalho visa apresentar informações que viabilizem a fabricação de componentes de rolamentos com limites superiores de resistência à fadiga, com a intenção de proporcionar uma vida útil maior ao rolamento, e, também, a otimização da fabricação das peças, dispensando em alguns casos o processo final e usual de retificação, o que implica uma redução de custos. As motivações deste estudo são a geração de altas tensões residuais compressivas no torneamento duro-seco a altas velocidades, a aplicação do RMB como técnica de medição das tensões residuais em aço 100CrMn6 e a otimização da qualidade/custos na fabricação de rolamentos. Para atingir essas metas, será estudada a influência dos parâmetros da usinagem (velocidade de corte (Vc), avanço (a), penetração (p) e desgaste da ferramenta (VB)) na geração das tensões residuais superficiais (sR) e sobre as forças de torneamento (Fc, Fa, Fp), em anéis internos de rolamentos cônicos de aço DIN 100CrMn6 endurecidos termicamente, procurando-se estabelecer uma correlação entre o desgaste da ferramenta e os referidos esforços e tensões residuais. Na etapa experimental, será utilizado um planejamento fatorial completo para executar os ensaios e medições projetadas. No ensaio de torneamento, serão medidas as forças de corte utilizando-se, para isso, um dinamômetro piezoelétrico. Em seguida, serão efetuadas medições de rugosidade. Também será realizado o estudo da microestrutura através da análise metalográfica. As tensões residuais serão medidas utilizando-se o método do furo-cego com extensometria elétrica, e as medidas das alterações microestruturais superficiais serão realizadas pela técnica do Ruído Magnético de Barkhausen (RMB). Serão correlacionados os valores de tensão residual obtidos pela técnica do furo com o RMB.
Título em inglês
Evaluation through the mgnetic inspection of the superficial condition of steel bearing rings DIN 100Cr6 after hard and dry turning.
Palavras-chave em inglês
Hard turning
High speed turning
Machining forces
Magnetic Barkhausen noise
Residual stress
Tool wear
Resumo em inglês
The present work presents information for the manufacturing of ball bearings components with higher limits of resistance to fatigue, enabling a longer useful life and also the optimization of the production of the pieces, making the usual and final process of grinding unnecessary, which would result in a costs reduction. The motivations of this study are the generation of compressive high residual stress in the hard-dry turning at high speeds, the application of the MBN as technique of measurement of the residual stress in steel 100CrMn6, and the optimization of the quality/costs in the manufacturing of ball bearings. In order to achieve these purpose, the work will study the influence of the machining parameters (cutting speed (Vc), feed rate (a), depth of cut (p), and wear of tool (VB)) in the generation of the superficial residual tensions and also the turning forces (Fc, Fa, Fp), in internal conical rings of ball bearings of steel 100CrMn6 thermally hardened, seeking to find a correlation between the stress of the tool and the referred efforts. In the experimental phase, a complete factorial planning will be used to perform the tests and measurements projected. In the turning tests, the cutting forces will be measured using a piezoelectric dynamometer. After that, measurements of superficial roughness will be performed. Also, the study of the microstructure will be made through the metallographic analysis. The residual tensions will be measured using the strain gage hole-drilling method and the measurement of the superficial microestrutural alterations will be carried out using the technical of the magnetic Barkhausen noise (MBN). The values of residual tension obtained by the hole-drilling will be correlated with the RMB.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Tese_Carlos.pdf (14.10 Mbytes)
Data de Publicação
2009-07-08
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.