Tese de Doutorado
DOI
10.11606/T.3.2007.tde-27072007-143816
Documento
Autor
Nome completo
Andréia Azeredo Nince
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2007
Orientador
Banca examinadora
Figueiredo, Antonio Domingues de (Presidente)
Agopyan, Vahan
Assis, André Pacheco de
Helene, Paulo Roberto do Lago
Nepomuceno, Antonio Alberto
Título em português
Lascamento do concreto exposto a altas temperaturas.
Palavras-chave em português
Altas temperaturas
Concreto
Concreto de alta resistência
Concreto reforçado com fibras
Fibras artificiais
Lascamento
Resumo em português
Esta pesquisa foi motivada pela existência de controvérsia na literatura sobre concreto exposto a altas temperaturas, das dúvidas ainda por solucionar acerca da matéria e da lacuna na norma brasileira para a matéria. Este tema reapareceu após os vários acidentes em túneis ao redor do mundo ocorridos nos últimos dez anos, nos quais se verificou a ocorrência de lascamento explosivo de forma intensa, afetando a estabilidade estrutural. O objetivo principal da tese é correlacionar os parâmetros tecnológicos de dosagem (relação água/cimento, teor de argamassa e consumo total de água) às condições de risco de lascamento, associados à umidade ambiente, que indiretamente, influencia no grau de saturação do concreto. O segundo objetivo é otimizar o uso de fibras de polipropileno para minimizar o efeito do lascamento. Adotou-se empregar a curva-padrão H durante 55 minutos em corpos-de-prova cúbicos aquecidos apenas em uma das fases com sua dilatação térmica lateral restringida. O nível de lascamento foi avaliado usando o volume lascado, obtido pela espessura medida diretamente nos corpos-de-prova, multiplicada pela área lascada, calculada pelo AUTOCAD 2000. Os resultados mostraram que o parâmetro tecnológico mais relevante na ocorrência de lascamento foi a relação água/cimento e a umidade ambiente apresentou capacidade de alterar as condições de risco de lascamento. No estudo com as fibras percebeu-se diferentes teores de fibras e diferentes características das fibras para cada grupo de a/c. Conclui-se que a relação água/cimento mais baixa associada a umidade a ambiente mais elevada é a condição mais propícia a ocorrência de lascamento. Conclui-se também que o teor de fibras de 600g/m³ é o teor mínimo para se reduzir o lascamento no grupo a/c=0,50 e 1750g/m³ no grupo a/c=0,25. A fibra L=12mm F=36µm PF=140°C mostrou-se a mais eficaz no grupo a/c=0,50 apenas o comprimento L=6 mm mostrou-se eficiente na redução do lascamento.
Título em inglês
Spalling of concrete exposed at high temperatures.
Palavras-chave em inglês
Concrete
Fiber
Fiber reinforced concrete
High temperature
High-strength concrete
Spalling
Resumo em inglês
The present research was motivated by the going controversy in the literature about concrete exposed to high temperatures, the yet unanswered doubts existent on this subject and in the absence of regulation on the matter in Brazil. The theme gained significance after the occurrence of several accidents in tunnels all over the world in the last ten years, in which were observed a very intense form of explosive spalling that affected structural stability of the sites. The main purpose of this work is set up a correlation between technological parameters of dosage in concrete (water cement rate -w/c, mortar content - a, and total water consumption - H) and risk conditions of spalling, which are related to environment humidity that indirectly effects concrete saturation level. The second goal is to optimize the use of polypropylene fiber in order to minimize spalling. The standard H curve was applied during 55 minutes in cubic samples with only a single surface exposed to heat and with restrained lateral thermo dilatation. The response variable was the observed volume of spalling (with multiplied by area of spalling in the sample). The results showed the rate water/cement as the most relevant technology parameter related to spalling risk conditions. Whereas the use of fiber is concerned, efficiency required different fiber content and characteristic for each water/cement rate combined with higher environment humidity provides proper conditions for the occurrence of spalling were 600g/m³ and 1750g/m³ for water/cement ratios of 0,5 and 0,25 respectively. It was also found that the fiber with L=12mm, F=36µm PF=140°C was the most effective in reducing spalling for a water/cement ratio of 0,50 whilst for a effective in reducing spalling for a water/cement ratio of 0,50 whilst for a water/cement ratio of 0,50 whilst for a water/cement ratio 0,25 only the length (L=6 mm) appeared as a significant factor.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
FICHACATALOGrev.doc (69.50 Kbytes)
Data de Publicação
2009-08-25
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.