Dissertação de Mestrado
DOI
10.11606/D.3.2011.tde-12032012-120653
Documento
Autor
Nome completo
Engler Apaza Medina
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2011
Orientador
Banca examinadora
Figueiredo, Antonio Domingues de (Presidente)
Cincotto, Maria Alba
Kihara, Yushiro
Título em português
Pozolanicidade do metacaulim em sistemas binários com cimento Portland e hidróxido de cálcio.
Palavras-chave em português
Cimento pozolânico
Concreto
Hidróxido de cálcio
Metacaulim
Pasta
Resumo em português
O metacaulim é um material pozolânico que vem sendo pesquisado e adotado em vários países. O metacaulim é constituído basicamente de sílica (SiO) e alumina (Al2O3) na fase amorfa, capaz de reagir com o hidróxido de cálcio Ca(OH) gerado durante a hidratação do cimento Portland, formando produtos hidratados similares aos decorrentes da hidratação direta do clinquer Portland. Esta pozolana acelera o processo de hidratação do cimento, formando silicato de cálcio hidratado (C-S-H) adicional. O conhecimento das características do metacaulim que influenciam a interação com a cal, se faz necessário para subsidiar medidas preventivas com relação ao consumo de portlandita. O presente trabalho visa determinar as características físico-químicas relevantes para o entendimento da atividade pozolânica, avaliando as reações propiciadas pelo metacaulim em sistemas binários. Para este propósito, realizaram-se estudos experimentais em pasta e concreto, usando as técnicas de difratometria de raios X e de termogravimetria. As etapas experimentais consistiram: na caracterização do metacaulim, com ênfase na determinação do teor da fase amorfa; a avaliação da cinética da reação em sistema metacaulim/hidróxido de cálcio e análise da evolução da hidratação de cimento com alto teor de metacaulim. Nos sistemas cimenticios de concretos com diferentes teores de substituição de metacaulim com e sem cal hidratada, foi avaliado o comportamento da resistência à compressão. No metacaulim estudado, o teor da fase amorfa foi de 74,60% e o restante (25,40%) atua como material inerte, e o consumo máximo por atividade pozolânica, foi de 1,34 gr de Ca(OH)/grama de fase amorfa de metacaulim. Na evolução das reações, por atividade pozolânica o C-S-H foi formando gradativamente. A adição de 15% de metacaulim e 5% de cal hidratada em concretos proporcionou um ganho de resistência de 17% a mais em função do concreto de referência.
Título em inglês
Pozzolanic metakaolin in the binary systems with Portland cement and calcium hidroxide.
Palavras-chave em inglês
Calcium hidroxide
Concrete
Metakaolin
Paste
Pozzolanic cement
Resumo em inglês
The metakaolin is a pozzolanic material that has been investigated and adopted in several countries. The metakaolin consists primarily of silica (SiO) and alumina (Al2O3) in the amorphous phase, and can react with calcium hydroxide Ca (OH) generated during hydration of Portland cement to form products similar to those obtained during Portland clinker basic hydration. This pozzolana could accelerate the hydration of cement, forming calcium silicate hydrate (C-S-H) additional. The knowledge of the characteristics of metakaolin that influence the interaction with lime provides the necessary subsidize to prevent excessive consumption of portlandite. This paper aims to determine the physical and chemical relevant characteristics in order to understand the pozzolanic activity, evaluating the responses provided by the metakaolin in binary systems. For this purpose, experimental studies were conducted in paste and concrete, using the techniques of X-ray diffraction and thermogravimetry. The experimental steps consisted of: the characterization of metakaolin, with emphasis on determining the amorphous phase content, this evaluation of the kinetics of the reaction system metakaolin and calcium hydroxide; The analysis of the evolution of the cement hydration with high content of metakaolin. In cementitious systems of concrete with different metakaolin replacement levels with and without hydrated lime, was rated the behavior of the compressive strength. The content of amorphous phase In the studied metakaolim was 74.60% and the remainder (25.40%) acts as an inert material, and the máximum consumption by pozzolanic activity was 1.34 g of Ca (OH)/g amorphous phase of metakaolin. During the evolution of pozzolanic reactions, the C-S-H was gradually formed. The addition of 15% metakaolin and 5% hydrated lime in concrete has a strength gain of 17% more depending on the reference concrete.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2012-04-09
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.