Dissertação de Mestrado
DOI
10.11606/D.3.2007.tde-08012008-142809
Documento
Autor
Nome completo
Otávio Filipe da Rocha
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2007
Orientador
Banca examinadora
Viana, Carlos Eduardo (Presidente)
Bonnaud, Olivier
Mansano, Ronaldo Domingues
Título em português
Caracterização de filmes finos de óxido de silício depositados em um reator HD-PECVD a partir de TEOS a ultra baixa temperatura.
Palavras-chave em português
Filmes finos
Plasma (microeletrônica)
Processos de microeletrônica
Resumo em português
Este trabalho reporta o estudo e desenvolvimento do processo de deposição química a vapor enriquecida por plasma de alta densidade de filmes finos de óxido de silício obtidos em ultra baixa temperatura, inferior a 100°C, tendo como fonte de silício o vapor de TEOS. O principal objetivo deste trabalho é, além da obtenção de filmes de óxido de silício com propriedades elétricas adequadas para utilização em TFTs, compreender os fenômenos que regem o processo de deposição química sob um plasma de alta densidade a partir da caracterização estrutural e elétrica de filmes depositados sob diferentes condições de processo, de modo a poder-se controlar as propriedades dos materiais obtidos. As técnicas de análise empregadas para a caracterização das amostras foram: elipsometria, FTIRS, RBS, curvas de taxa de deposição e corrosão, curvas capacitância versus tensão de alta freqüência, curvas corrente elétrica versus tensão. Os principais resultados obtidos através da caracterização elétrica de capacitores MOS com área 9 x 10-4 cm-2, construídos a partir dos filmes de SiOx depositados, são: VFB = -3,94 V; eOX = 3,92; QSS/q = 6,08×1011 cm-2; EBD = 9,44 MV/cm e JLK = 2,50×10-7 A/cm-2 @ 4 MV/cm.
Título em inglês
Characterization of silicon dioxide thin films deposited in a HD-PECVD reactor from TEOS at ultra low temperature.
Palavras-chave em inglês
Microelectronic processes
Plasma (microelectronic)
Thin films
Resumo em inglês
This work reports on the results obtained from high-density plasma enhanced chemical vapor deposited silicon oxide films at ultra low temperature, i.e. 30°C, using TEOS vapor as the silicon source oxidized with assistance of argon. The objectives of this work are: first, understand the phenomena that conducts the chemical vapor deposition in high density regime in order to control the deposited silicon oxide films properties, and also obtain silicon oxide films with adequate properties, from structural and electric characterization of films deposited under different process conditions, in order to control the properties of the deposited materials, for use in TFT's technology. Different analysis techniques were applied to characterize the deposited layers: ellipsometry, FTIRS, RBS, deposition and etch rate curves, capacitance versus voltage in high-frequency curves and electric current versus voltage curves. Obtained results were presented and subdivided in accordance with TEOS flow used in the deposition process: 0,5 sccm (for temperatures of 30, 150 and 250°C), 1 and 4 sccm. Characterization results were obtained by the different techniques employed suggests the adequate control of the silicon oxide films characteristics according HD-PECVD/TEOS process parameters which are: stoichiometry, density, Si-H and Si-OH bonds content, position of Si-O peak and absence of organic contamination. The main results obtained from the electric characterization MOS capacitors with area 9 x 10-4 cm-2, implemented with deposited SiOx films, are: VFB = -3,94 V; eOX = 3,92; QSS/q = 6,08×1011 cm-2; EBD = 9,44 MV/cm and JLK = 2,50×10-7 A/cm-2 @ 4 MV/cm.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2008-02-29
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.