Dissertação de Mestrado
DOI
10.11606/D.25.2004.tde-21032005-152154
Documento
Autor
Nome completo
Miguel Alberto de Jesus Asenjo Martinez
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Bauru, 2004
Orientador
Banca examinadora
Mondelli, Rafael Francisco Lia (Presidente)
Franco, Eduardo Batista
Martins, Luis Roberto Marcondes
Título em português
Avaliação do desgaste e da rugosidade superficial de uma resina composta, após escovação simulada, em função de diferentes energias e fontes de luz usadas na polimerização
Palavras-chave em português
dentística
polimerização
resinas compostas
Resumo em português
Avaliou-se in vitro o desgaste e a rugosidade superficial da resina composta FiltekTM Z-250 (3M/ESPE), após escovação simulada, em função de diferentes energias e fontes de luz usadas na polimerização. Foram utilizadas duas fontes de luz: halógena (VIP/BISCO) e LED (Ultrablue IS / DMC equipamentos). Uma matriz de aço inoxidável foi empregada na obtenção de quarenta corpos-de-prova (15X5mm) divididos em 4 grupos: G1: VIP 300mW/cm2 x 20s; G2 = VIP 600mW/cm2 x 20s; G3: LED 300mW/cm2 x 20s e G4: LED 600mW/cm2 x 20s. A metade de cada corpo-de-prova foi protegida e a outra metade submetida a 200.000 ciclos de escovação, utilizando-se escovas dentais (Kolynos) e pasta dental (Colgate), diluída em água deionizada. O desgaste foi determinado após a realização de 5 leituras para cada espécime. O rugosímetro foi utilizado para verificar as diferenças entre o perfil real entre as duas superfícies. A alteração da rugosidade superficial (Ra) foi determinada pela diferença entre a média de cinco leituras iniciais (antes da escovação) e de cinco finais (após escovação). Os resultados foram submetidos à análise de variância a dois critérios e teste de Tukey (p<0,05). O desgaste apresentado foi: G1: 13,96±0,756µm (B); G2; 10,90±0,507µm (A); G3: 34,63±1,931µm (C) e G4; 12,95±0,510µm (B). As diferenças da rugosidade superficial (Ra) foram: G1: 0,923±0,031µm (B); G2: 0,891±0,036µm (A); G3: 1,031±0,019µm (C) and G4: 0,918±0,032µm (B). De forma geral, a fonte de luz halógena proporcionou melhor comportamento físicomecânico da resina composta avaliada em comparação a fonte de luz LED com mesma energia de ativação.
Título em inglês
Evaluation of wear and superficial roughness of a composed resin, after simulated brushing, in function of different energies and sources of light used in the polymerization
Resumo em inglês
An in vitro study was conducted for evaluation of wear and surface roughness of the composite resin FiltekTM Z-250 (3M/ESPE) after simulated toothbrushing, according to different light energies and sources employed for curing. Two light sources were employed, namely halogen (QTH) (VIP/BISCO) and LED (Ultrablue IS / DMC Equipments). A stainless steel template was used to obtain forty specimens (15X5mm) divided into 4 groups: G1 = QTH 300mW/cm2 x 20s; G2 = QTH 600mW/cm2 x 20s; G3 = LED 300mW/cm2 x 20s and G4 = LED 600mW/cm2 x 20s. Half of the each specimens was protected, and the other half was submitted to 200,000 brushstrokes using toothbrushes (Kolynos) and dentifrice (Colgate) diluted in deionized water. Wear was established after accomplishment of 5 readings for each specimen. The roughness meter was employed for observation of differences in the actual profile between the two surfaces. The alteration in surface roughness (Ra) was calculated by the difference between the mean of the five initial readings (before toothbrushing) and five final readings (after toothbrushing). The results were submitted to a two-way analysis of variance and to the Tukey test (p<0.05). The wear rates observed were: G1: 13.96±0.756µm (B); G2: 10.90±0.507µm (A); G3: 34.63±1.931µm (C) and G4: 12.95±0.510µm (B). The differences in surface roughness (Ra) were: G1: 0.923±0.031µm (B); G2: 0.891±0.036µm (A); G3: 1.031±0;019µm (C) and G4: 0.918±0.032µm (B). In general, the QTH curing unit provided better physicomechanical performance of the composite resin compared to the LED curing unit with the same activation energy.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2005-04-04
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.