Dissertação de Mestrado
DOI
10.11606/D.23.1997.tde-30052006-150344
Documento
Autor
Nome completo
Alessandro Leite Cavalcanti
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 1997
Orientador
Banca examinadora
Chelotti, Adolpho (Presidente)
Fazzi, Ronaldo
Turbino, Miriam Lacalle
Título em português
Avaliação 'in vitro' da Microinfiltração na Interface da Parede Gengival das Caixas Proximais em Cavidades Classe II de Molares Decíduos, Restaurados com Resina Composta Auto e Fotopolimerizável
Palavras-chave em português
dente decíduo
microinfiltração
resina composta
Resumo em português
A finalidade deste estudo foi avaliar “in vitro” a microinfiltração marginal presente na interface da parede gengival de cavidades classe II em molares decíduos, restaurados com resina composta (auto e fotopolimerizável), com a utilização de uma solução corante. Os preparos cavitários apresentavam a parede gengival em esmalte, sendo restaurados segundo 4 diferentes técnicas: resina composta fotopolimerizável; resina composta autopolimerizável; técnica mista (resina composta auto e fotopolimerizável) e ionômero de vidro/resina composta. Em seguida, procedeu-se à ciclagem térmica (5oC e 55oC, 700 ciclos), impermeabilização, imersão em solução corante e seccionamento. A avaliação quanto à microinfiltração, foi feita seguindo-se uma escala preestabelecida (graus de 0 a 4). Após a análise estatística dos resultados, concluiu-se que todos os grupos apresentaram microinfiltração, em graus variados, todavia os grupos que utilizaram a técnica mista e o ionômero/resina fotopolimerizável apresentaram os menores graus de infiltração, e que não se observou microinfiltração na interface resina composta autopolimerizável/fotopolimerizável.
Título em inglês
ANALYSIS “IN VITRO” OF MICROLEAKINGS ON GUM’S EDGES OF THE APPROXIMAL BOXES IN CLASS II CAVITIES OF DECIDUOUS MOLARS, RESTORED WITH AUTO AND LIGHT-CURED COMPOSITE RESIN
Palavras-chave em inglês
composite resin
deciduous tooth
microleakage
Resumo em inglês
The purpose of this study was evaluation “in vitro” of marginal microleakings, present on gum’s edges of class II cavities of deciduous molars, restored with composite resin (auto and light-cured), with the use of a staining solution to verify the leaking. Cavities prepared presented enamel on gum’s edges and were restored according to four different techniques: lightcured composite resin; auto-cured composite resin; mixed technique (auto and light-cured composite resin) and glass-ionomer/composite resin. Next, we proceeded to thermo-cycling (5°C and 55°C, 700 cycles), turning impermeable, immersion in staining solution and slicing. The microleaking evaluation was done according to a pre-established scale (from 0 a 4 degrees). After the statical analysis of the results, it was concluded that all the groups presented microleaking, in varying degrees. However, the groups which used the mixed technique and light-cured resin presented the smallest levels of leaking, and microleaking was not observed on the auto-cured composite resin/light-cured composite resin edge.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Dissertacao.pdf (783.21 Kbytes)
Data de Publicação
2006-06-20
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.