Dissertação de Mestrado
DOI
10.11606/D.18.2018.tde-23052018-105250
Documento
Autor
Nome completo
Felipe Henrique Santa Maria
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2018
Orientador
Banca examinadora
Oliveira, Marcelo Falcão de (Presidente)
Ishikawa, Tomaz Toshimi
Marques, Paulo Wilmar Barbosa
Título em português
Análise térmica da influência do oxigênio na amorfização de ligas baseadas em Cu-Zr
Palavras-chave em português
Análises térmicas
Cristalização
Cu-Zr
Oxigênio
Vidros metálicos
Resumo em português
Os vidros metálicos baseados em Cu-Zr representam uma classe bastante promissora para a categoria de materiais estruturais, tendo em vista suas interessantes propriedades resultantes da natureza amorfa. Sabe-se que o oxigênio tem grande influência na formação da estrutura amorfa e consequentemente nas propriedades dessa classe de materiais. No presente trabalho, ligas amorfas baseadas em Cu-Zr foram analisadas termicamente a fim de se observar o comportamento das mesmas frente à contaminação com oxigênio. As análises térmicas foram realizadas em um equipamento de calorimetria exploratória diferencial (DSC), e as temperaturas características como de transição vítrea, cristalização, fusão e líquidus foram determinadas. Concluiu-se que conforme a literatura apresenta, o processo de cristalização é favorecido pela presença de oxigênio, causando uma queda na energia de ativação dos processos de cristalização das ligas trabalhadas. Através de ensaios que simularam tratamentos térmicos, cristalizou-se controladamente as amostras amorfas baseadas em Cu-Zr a fim de formar compósitos entre cristais e vidros metálicos buscando diminuir a fragilidade das ligas.
Título em inglês
Thermal analysis of oxygen influence on the amorphization of Cu-Zr-based alloys
Palavras-chave em inglês
Bulk metallic glasses
Crystallization
Cu-Zr
Oxygen
Thermal analysis
Resumo em inglês
Cu-Zr-based bulk metallic glasses represent a very promising class of structural materials with interesting properties resulting from the amorphous nature. It is known that oxygen has a great influence on the formation of the amorphous structure and consequently on the properties of these materials. In the present work, Cu-Zr-based amorphous alloys were thermally analyzed in order to observe their behavior against oxygen contamination. Thermal analyzis were performed on a differential scanning calorimetry (DSC) equipment, and characteristic temperatures as glass transition, crystallization, melting and liquidus were determined. It was concluded that, according to the literature, the crystallization process is favored by the presence of oxygen, causing a decrease in the activation energy of the crystallization processes of the worked alloys. Through tests that simulated heat treatments, the amorphous samples were crystallized in order to form composites between crystals and metallic glasses in order to reduce the brittleness of the alloys.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2018-07-13
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.