Mémoire de Maîtrise
DOI
Document
Auteur
Nom complet
Thiago Romanelli Theodoro
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2018
Directeur
Jury
Aguiar, Leandro Gonçalves de (Président)
Freitas, Larissa de
Pereira, Félix Monteiro
Soares Neto, Turíbio Gomes
Titre en portugais
Modificação química de resinas à base de estireno através do processo de sulfonação: estudo experimental e modelagem matemática
Mots-clés en portugais
Catalisador
Modelagem
Resina polimérica
Sulfonação
Resumé en portugais
A proposta deste trabalho consistiu em realizar o estudo experimental e matemático do processo de sulfonação de resinas estirênicas reticuladas com etileno-glicol dimetacrilato (PS-EGDMA) e trietileno-glicol dimetacrilato (PS-TEGDMA). O processo de sulfonação de resinas estirênicas é uma das modificações químicas mais utilizadas na indústria e permite conferir características como seletividade às resinas, favorecendo seu uso em diversos processos. Foi utilizado um planejamento de Taguchi L9 com os fatores: fração monomérica, fração de agentes reticulantes e fração de solventes inertes (tolueno e heptano), referentes ao processo de polimerização. As resinas produzidas foram utilizadas na sulfonação, na qual a temperatura foi variada para determinar o ponto ótimo em termos de capacidade de troca iônica e variação de massa. Por meio de balanços de massa e fazendo o uso do modelo do núcleo não reagido foi feita a modelagem matemática do processo. Os resultados obtidos mostram que as resinas reticuladas com etileno-glicol dimetacrilato (EGDMA) e trietileno-glicol dimetcrilato (TGDMA) apresentam boa capacidade de troca iônica (CTI) quando comparadas às resinas comerciais de estireno-divinilbenzeno (S-DVB), como, por exemplo, a Amberlyst®. As partículas sulfonadas de PS-EGDMA apresentaram CTI de 3,988 meq/g com ganho de massa de 30% enquanto as de PS-TEGDMA apresentaram capacidade de 3,477meq/g com ganho de massa de 47% no ponto ótimo tendo sido produzidas com temperaturas de sulfonação de 57,5ºC e 65ºC respectivamente. O modelo desenvolvido apresentou bom ajuste no intervalo entre o início da reação e o ponto máximo de capacidade de troca iônica, sendo capaz de prever as constantes cinéticas e de difusão da reação. Além disso, as partículas produzidas foram testadas na catálise heterogênea e conversões acima de 78% foram obtidas mostrando-se um eficiente catalisador.
Titre en anglais
Chemical modification of styrenic resins by sulfontation process: experimental and mathematical modelling
Mots-clés en anglais
Catalyst
Modeling
Polymer resin
Sulfonation
Resumé en anglais
The purpose of this work was to carry out the experimental and mathematical study of the sulfonation process of styrenic resins cross-linked with ethylene glycol dimethacrylate (EGDMA) and triethylene glycol dimethacrylate (TEGDMA). The sulfonation process of styrenic resins is very used in industry and allows particles to achieve characteristics like selectivity, favoring its use in several processes. It was used Taguchi L9 experimental design with the following factors: monomer molar fraction, fraction of crosslinking agents and fraction of inert solvents (toluene and heptane), referring to the polymerization process. The resins produced were used in the sulfonation process, in which the temperature was varied to determine the optimum point in terms of ion exchange capacity and mass variation. Mass balances and the unreacted core model were in order to develop the mathematical model. The results showed that PS-EGDMA and PS-TGDMA crosslinked resins exhibit good ion exchange capacity when compared to styrene-divinylbenzene (S-DVB) commercial resins, such as Amberlyst®. The sulfonated PS-EGDMA particles showed ion exchange capacity of 3,988 meq/g with a mass gain of 30% while those of PS-TEGDMA presented a capacity of 3,477meq/g with mass gain of 47% at the optimum point and were produced with sulfonation temperatures of 55.7ºC and 65ºC respectively. The developed mathematical model showed a good fit in the interval between the beginning of the reaction and the maximum point of ion exchange capacity, being able to predict the kinetic and diffusion constants of the reaction. In addition, the produced particles were tested in the heterogeneous catalysis and conversions above 78% were obtained proving an efficient catalyst.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EQD18002_O.pdf (2.56 Mbytes)
Date de Publication
2019-07-12
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2023. Tous droits réservés.