Disertación de Maestría
DOI
https://doi.org/10.11606/D.97.2011.tde-27082013-103950
Documento
Autor
Nombre completo
Jaime Caetano Cazotti
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2011
Director
Tribunal
Santos, Amilton Martins dos (Presidente)
Moreira, José Carlos
Shigue, Carlos Yujiro
Título en portugués
Síntese e caracterização de látices híbridos de poli(acetato de vinila)/montmorilonita - PVAc/MMT para aplicação como adesivos
Palabras clave en portugués
Adesivos
Látices Híbridos
Montmorilonita
Nanocompósitos
Poli(acetato de vinila)
Polimerização em Emulsão
Resumen en portugués
Este projeto de mestrado teve como objetivo a obtenção de látices híbridos constituídos de poli(acetato de vinila) (PVAc) e argila montmorilonita (MMT). O homopolímero de acetato de vinila foi sintetizado através da técnica de polimerização em emulsão na presença de diferentes tipos de argila, sendo empregada uma argila sódica (Na-MMT) e três argilas modificadas (o-MMT) com diferentes sais quaternários de amônio. Poli(álcool vinílico) (PVOH) foi utilizado como colóide protetor e persulfato de amônio (APS) como iniciador. Foi estudada a melhor condição para incorporação da argila na matriz polimérica, visando a esfoliação desta nanocarga, resultando desta maneira na formação de nanocompósitos com propriedades diferenciadas. A influência da presença das argilas foi avaliada em termos da velocidade de consumo de monômero, a qual foi acompanhada por gravimetria. Os látices foram caracterizados quanto ao diâmetro médio de partícula e polidispersidade pela técnica de espalhamento de luz (LS). O teor de coágulos do látex foi calculado por análise gravimétrica e a viscosidade analisada em um viscosímetro rotacional. Os filmes nanocompósitos foram caracterizados pelas técnicas de análise dinâmico-mecânica (DMA), análise termogravimétrica (TGA) e difração de raios X (DRX). A morfologia das partículas de látex foi avaliada por microscopia eletrônica de transmissão (MET).
Título en inglés
Synthesis and characterization of poly(vinyl acetate)/montmorillonite - PVAc/MMT hybrid latexes for use as adhesives
Palabras clave en inglés
Adhesives
Emulsion Polymerization
Hybrid Latexes
Montmorillonite
Nanocomposites
Poly(vinyl acetate)
Resumen en inglés
The goal of this project was the preparation of hybrids latexes constituted by poly(vinyl acetate) (PVAc) and montmorillonite (MMT) clays. The poly(vinyl acetate) homopolymer was synthesized via emulsion polymerization in the presence of different types of clay, one sodium clay (Na-MMT) and organically modified clays (o-MMT) with different ammonium quaternary salts. Poly(vinyl alcohol) (PVOH) was used as protective colloid and ammonium persulfate (APS) as initiator. It was evaluated the best condition for the incorporation of the clay in the polymeric matrix, looking forward the exfoliation of the nanofiller, resulting in the formation of nanocomposites with new and improved properties. The influence of clay type and loading was evaluated in terms of latex stability and monomer consumption rate. The latexes were characterized in terms of particle size diameter and polydispersity by light scattering (LS) technique. Coagulum content was determined by gravimetric analysis and viscosity was analyzed in a rotational viscometer. Nanocomposite films were characterized by dynamic-mechanical analysis (DMA), thermogravimetric analysis (TGA) and X-ray diffraction (XRD). Latex particles morphology was evaluated by transmission electron microscopy (TEM).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EQD11010.pdf (2.04 Mbytes)
Fecha de Publicación
2013-08-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.