Disertación de Maestría
DOI
https://doi.org/10.11606/D.97.2020.tde-29042022-101321
Documento
Autor
Nombre completo
Leandro Rodrigues de Faria
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2020
Director
Tribunal
Machado, Antonio Jefferson da Silva (Presidente)
Bittar, Eduardo Matzenbacher
Eleno, Luiz Tadeu Fernandes
Luz, Mário Sérgio da
Título en portugués
Investigação da supercondutividade no carbeto quaternário YRe2iC
Palabras clave en portugués
Carbetos
Intermetálicos
Multibandas
Supercondutividade
Resumen en portugués
Carbetos quaternários, em especial a classe dos borocarbetos, vêm chamado grande atenção devido a sua ampla variedade de propriedades únicas. Como alternativa a estes compostos, o presente trabalho vem apresentar supercondutividade no carbeto quaternário YRe2SiC. Amostras de composição nominal YRe2SiC e foram preparadas em forno a arco e resfriadas em diferentes taxas. Suas microestruturas foram analisadas, e as propriedades supercondutoras da melhor amostra foram estudadas, revelando Tc de aproximadamente 5,9 K. O comportamento de Hc1(T) e Hc2(T) são similares ao de materiais não convencionais como YNi2B2C e MgB2, e anomalias nas medidas calorimétricas levantam indícios de comportamento não-usual neste carbeto. Em outras palavras, os resultados apresentados neste trabalho sugerem que este tipo de carbeto quaternário de baixa simetria possa exibir o comportamento de um material multibandas.
Título en inglés
Investigation of superconductivity in the quaternary carbide YRe2SiC
Palabras clave en inglés
Carbides
Intermetallics
Multiband
Superconductivity
Resumen en inglés
Quaternary carbides, specially the borocarbides, have been receiving great attention due to their great variety of unique properties. As an alternative to these compounds, the current work reports superconductivity in the quaternary carbide YRe2SiC. Samples of nominal composition YRe2SiC were arc-melted and cooled in different rates. Their microstructures were analyzed and the superconducting properties of the best sample were studied, revealing a Tc close to 5.9 K. The behavior of Hc1(T) and Hc2(T) are reminiscent to unconventional superconductors YNi2B2C and MgB2, and anomalies in the calorimetric measurements bring evidences of a non-usual behavior in this carbide. In other words, the results shown in this work reveal that this type of low-symmetry quaternary carbide may be an example of a new multiband material.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD20002_O.pdf (1.93 Mbytes)
Fecha de Publicación
2022-04-29
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2023. Todos los derechos reservados.