Disertación de Maestría
DOI
Documento
Autor
Nombre completo
Danyela Cardoso Carvalho
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2018
Director
Tribunal
Machado, Antonio Jefferson da Silva (Presidente)
Bittar, Eduardo Matzenbacher
Chaia, Nabil
Santos, Carlos Alberto Moreira dos
Título en portugués
Investigação da supercondutividade em compostos do sistema Zr-V-Ga
Palabras clave en portugués
Intermetálicos
Multibanda
Supercondutividade
Zr-V-Ga
Resumen en portugués
Este trabalho teve como objetivo a investigação de novos materiais promissores para a supercondutividade presentes no sistema ternário do Zr-V-Ga. Os resultados apresentados de magnetização, resistividade e calor específico, mostram de forma inequívoca que o Zr3V2Ga4 é um novo material supercondutor com temperatura crítica de transição supercondutora nas proximidades de 14,3K. O estudo do composto ZrV2Ga4 mostrou que a supercondutividade é revelada com temperatura crítica de aproximadamente 14,2 K. Medidas de calor especifico realizadas nessas amostras evidenciam de forma clara manifestações de supercondutores multibandas. Outra investigação importante realizada foi a substituição parcial de vanádio por titânio na estequiometria do composto ZrV2Ga4 representado pela composição global ZrV2-xTixGa4, revela que a substituição parcial de vanádio por titânio suprime a supercondutividade neste composto. Isto é mais evidente quando a substituição total de V por Ti suprime totalmente o comportamento supercondutor. Estes resultados sugerem que a supercondutividade pode ser dependente da unidade aniônica [V2Ga4]4-. Finalmente, esta dissertação mostra que o sistema ternário Zr-V-Ga é bastante rico em fases supercondutoras ainda não reportadas na literatura.
Título en inglés
Investigation of superconductivity in compounds of the Zr-V-Ga system
Palabras clave en inglés
Intermetallic
Multiband
Superconductivity
Zr-V-Ga
Resumen en inglés
This work aimed to investigate new promising materials for superconductivity present in the ternary system of Zr-V-Ga. The presented results of magnetization, resistivity and specific heat, show unequivocally that the Zr3V2Ga4 is a new superconducting material with critical temperature of superconducting transition close to 14.3K. The study of compound ZrV2Ga4 showed that superconductivity is revealed at a critical temperature of approximately 14.2K. Specific heat measurements carried out on these samples clearly demonstrate manifestations of multiband superconductors. Another important investigation carried out was the partial substitution of vanadium by titanium in the stoichiometry of the ZrV2Ga4 compound represented by the global composition ZrV2-xTixGa4, reveals that the partial substitution of vanadium by titanium suppresses the superconductivity in this compound. This is most evident when the total substitution of V for Ti totally suppresses the superconducting behavior. These results suggest that superconductivity may be dependent on the anionic unit [V2Ga4]4-. The results presented in this dissertation reveal that the ternary system Zr-V-Ga is rich in new superconducting materials not reported yet.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD18006_C.pdf (2.39 Mbytes)
Fecha de Publicación
2019-05-28
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.