Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.97.2021.tde-14062022-111350
Document
Auteur
Nom complet
Thomas Conte Machado
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2021
Directeur
Jury
Machado, Antonio Jefferson da Silva (Président)
Bortolozo, Ausdinir Danilo
Eleno, Luiz Tadeu Fernandes
Torikachvili, Milton Starosta
Titre en portugais
Avaliação do efeito de átomos intersticiais como boro e hidrogênio na indução de supercondutividade nos intermetálicos binários ZrAl2 e ZrAl3
Mots-clés en portugais
Dopagem
Intersticiais
Supercondutividade
ZrAl2
ZrAl3
Resumé en portugais
A dopagem de materiais, que são experimentalmente identificados como condutores tradicionais ou isolantes, tem trazido à tona novas perspectivas acerca do tema. Estudos revelaram a indução de supercondutividade nestes materiais não supercondutores, em decorrência do processo de dopagem. A supercondutividade que emerge após dopagem com elementos intersticiais como o boro e o carbono em matrizes que não são supercondutoras tais como o diamante, SiC, Si e Nb5Ge3, despertou grande interesse para este trabalho. Neste sentido, este trabalho traz um estudo de supercondutividade em ligas intermetálicas de composições ZrAl2 e ZrAl3, ligas estas não supercondutoras, que emerge com dopagem de boro e hidrogênio. Os compostos ZrAl2 e ZrAl3 foram ambos dopados com boro. Por outro lado, apenas o ZrAl2 foi dopado com hidrogênio. Os resultados com o ZrAl2 dopado com B, composto com estequiometria ZrAl1,9B0,1, forneceram indícios de uma transição supercondutora com TC próximo de 4,0K. Da mesma maneira, indícios de supercondutividade com temperatura crítica próxima de 5,8K foram verificadas na fase ZrAl3 dopado com B. A dopagem da fase ZrAl2 com hidrogênio (ZrAl2Hx), resultou em diferentes comportamentos e com temperaturas críticas próximas de 7,8K e 9,1K. Finalmente, será mostrado um resultado de supercondutividade em ZrAl2Hx, hidrogenada a partir do pó, com a surpreendente temperatura crítica de 37,5K.
Titre en anglais
Evaluation of the effect of interstitial atoms such as boron and hydrogen on the induction of superconductivity in the binary intermetallic ZrAl2 and ZrAl3
Mots-clés en anglais
Doping
Interstitials
Superconductivity
ZrAl2
ZrAl3
Resumé en anglais
The doping of materials, which are experimentally well known as traditional or insulating conductors, has brought up new perspectives on the subject. Studies have revealed the induction of superconductivity in these non-superconducting materials as a result of the doping process. The superconductivity thar emerges after doping with interstitial elements such as boron and carbon in matrices that are not superconducting such as diamond, SiC, Si and Nb5Ge3, aroused great interest for this work. Initially with boron and then the possibility of adding hydrogen as interstitial was envisioned, the results of which were motivating. Thus, this work this brings a study of superconductivity in intermetallic alloys of ZrAl2 and ZrAl3 composition, these non-superconducting alloys, which emerges with boron and hydrogen doping. The ZrAl2 and ZrAl3 compound were both doped with boron. On the other hand, ZrAl2 was doped only with hydrogen. The results of B doped ZrAl2, in the compound with ZrAl1,9B0,1 stoichiometry, provided evidence of a superconducting transition with TC close to 4,0K. Likewise, signs of superconductivity with critical temperature close to 5,8K was verified in the ZrAl3 doped with B. The hydrogen doping of ZrAl2 phase (ZrAl2Hx) resulted in different behavior and critical temperatures close to 7,8K and 9,71K. Finally is shown, a result of superconductivity in ZrAl2Hx, hydrogenized from the powder, with an amazing critical temperature of 37,5K
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EMD21003_O.pdf (9.78 Mbytes)
Date de Publication
2022-06-14
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2023. Tous droits réservés.