Doctoral Thesis
DOI
10.11606/T.97.2017.tde-30062017-203112
Document
Author
Full name
Rodrigo Duarte Silva
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Lorena, 2017
Supervisor
Committee
Santos, Amilton Martins dos (President)
Saron, Clodoaldo
Florenzano, Fábio Herbst
Giudici, Reinaldo
Oliveira, Mauricio Pinheiro de
Title in Portuguese
Encapsulação de montmorilonita por meio da polimerização radicalar controlada via RAFT em emulsão para produção de filmes nanoestruturados com propriedades anisotrópicas
Keywords in Portuguese
Encapsulação
Montmorilonita
Nanocompósitos poliméricos
Polimerização em emulsão
RAFT
Abstract in Portuguese
Este trabalho descreve a síntese de látices poliméricos híbridos contendo a argila natural Montmorilonita (MMT) por meio da polimerização radicalar controlada via mecanismo de transferência reversível de cadeia por adição-fragmentação (RAFT) em emulsão sem adição de surfatante. Primeiramente, copolímeros anfifílicos com diferentes estruturas e composições, foram preparados por meio da polimerização via RAFT em solução e caracterizados por ressonância magnética nuclear de hidrogênio (RMN 1H) e cromatografia por exclusão de tamanho (SEC). A interação entre os copolímeros sintetizados, chamados de macroagentes RAFT, e a superfície da MMT foi estudada por meio de isotermas de adsorção experimentais, as quais foram ajustadas por modelos teóricos. Os macroagentes RAFT à base de ácido acrílico (AA), acrilato de metil éter poli(etileno glicol) (PEGA) e acrilato de n-butila (BA) apresentaram afinidade pela argila como mostraram as isotermas do "tipo L" (Langmuir) obtidas. Os látices híbridos preparados utilizando esses macroagentes RAFT foram analisados por microscopia eletrônica de transmissão em temperatura criogênica (cryo-TEM), que revelou lamelas de MMT decoradas com nanopartículas poliméricas. As isotermas de adsorção dos macroagentes RAFT catiônicos à base de metacrilato de 2-(dimetilamino)etila (DMAEMA), PEGA e BA foram do "tipo H" (alta afinidade). Esses macroagentes RAFT possibilitaram a preparação de dispersões estáveis de complexos de MMT/macroagente RAFT, o que foi verificado por espalhamento dinâmico de luz (DLS), e sua utilização na síntese de látices híbridos levou à formação de uma camada polimérica em torno das lamelas de MMT. Os filmes poliméricos nanocompósitos obtidos a partir de látices catiônicos estáveis de poli(metacrilato de metila-co-acrilato de n-butila)/MMT apresentaram melhor estabilidade térmica e melhores propriedades mecânicas do que os filmes poliméricos preparados sem adição de argila como mostraram, respectivamente, os resultados de análise termogravimétrica (TG) e de análise termodinâmico-mecânica (DMA) dos materiais.
Title in English
Encapsulation of Montmorillonite by RAFT-mediated emulsion polymerization for the preparation of nanostructured films with anisotropic properties
Keywords in English
Emulsion polymerization
Encapsulation
Montmorillonite
Polymer nanocomposites
RAFT
Abstract in English
This work describes the synthesis of hybrid polymer latexes containing natural Montmorillonite clay (MMT) by reversible addition-fragmentation chain transfer (RAFT)-mediated surfactant-free emulsion polymerization. Firstly, amphiphilic copolymers with different structures and compositions were prepared by RAFT polymerization in solution and characterized by hydrogen nuclear magnetic resonance (1H NMR) and size exclusion chromatography (SEC). The interaction between these copolymers (referred to as macroRAFT agents) and the MMT surface was studied by experimental adsorption isotherms, which were adjusted by theoretical adsorption models. MacroRAFT agents based on acrylic acid (AA), poly(ethylene glycol) methyl ether acrylate (PEGA) and n-butyl acrylate (BA) displayed affinity for MMT as shown by the "L-type" (Langmuir) isotherms obtained. The hybrid latexes prepared using these macroRAFT agents were analyzed by transmission electron microscopy at cryogenic temperatures (cryo-TEM), which revealed polymer-decorated MMT platelets. The adsorption isotherms of cationic macroRAFT agents based on 2-(dimethylamino)ethyl methacrylate (DMAEMA), PEGA and BA were of the "H-type" (high affinity). These RAFT macroRAFT agents allowed the preparation of stable dispersions of MMT/macroRAFT agents complexes, which was verified by dynamic light scattering analysis (DLS), and their use in the synthesis of hybrid latexes led to the formation of a polymer layer surrounding the MMT platelets. Nanocomposite films obtained from stable cationic latexes of poly(methyl methacrylate-co-n-butyl acrylate)/MMT showed better thermal stability and better mechanical properties than polymer films prepared without addition of clay as shown, respectively, by the results of thermogravimetric analysis (TG) and dynamic mechanical analysis (DMA) of the final materials.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
EMT17001_C.pdf (10.90 Mbytes)
Publishing Date
2017-06-30
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2022. All rights reserved.