Tesis Doctoral
DOI
10.11606/T.97.2009.tde-27092012-123519
Documento
Autor
Nombre completo
Heide Heloise Bernardi
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2009
Director
Tribunal
Sandim, Hugo Ricardo Zschommler (Presidente)
Baptista, Carlos Antonio Reis Pereira
Barboza, Miguel Justino Ribeiro
Ferrante, Maurizio
Rios, Paulo Rangel
Título en portugués
Processamento e caracterização microestrutural de nióbio deformado plasticamente por extrusão em canal angular
Palabras clave en portugués
Deformação Plástica Severa
EBSD
ECAE
Nióbio
Recristalização
Textura
Resumen en portugués
Amostras de nióbio de alta pureza na forma de monocristais, bicristais e policristais foram retiradas de seções longitudinais de lingotes fundidos por feixe eletrônico. As amostras foram deformadas via extrusão em canal angular (ECAE - Equal Channel Angular Extrusion) em temperatura ambiente até 8 passes, utilizando a rota Bc numa matriz com ângulo de intersecção entre os canais de  = 90º. As amostras foram caracterizadas em termos da evolução microestrutural e da textura de deformação. A caracterização microestrutural foi realizada com o auxílio de microscopias ótica, eletrônica de varredura e eletrônica de transmissão, além de medidas de difração de elétrons retroespalhados (EBSD) para determinação da microtextura e da mesotextura. Medidas de microdureza Vickers foram realizadas para acompanhar o encruamento e o amolecimento das amostras. Um outro monocristal de nióbio foi deformado em 1 passe via ensaio interrompido, utilizando uma matriz com ângulo  = 120º, a fim de estudar a evolução da textura durante a passagem pelo canal de ECAE. A textura foi determinada por meio de difração de raios X e comparada com os dados da literatura para materiais deformados via ECAE com estrutura CCC e também com as texturas simuladas pelo modelo VPSC (visco-plastic self-consistent). No estudo comparativo numa escala maior (monocristal e policristal), verificou-se que houve um refinamento microestrutural significativo após 8 passes. O espaçamento médio entre os contornos de alto ângulo medido perpendicular à direção de extrusão foi próximo nos dois casos (500 nm), maior que o observado para o monocristal deformado numa escala menor (440 nm). Os resultados mostram ainda que os grãos do policristal deformado são mais equiaxiais que os do monocristal. Amostras foram recozidas isotermicamente para avaliar o comportamento frente ao engrossamento microestrutural. Os resultados mostram que o engrossamento torna-se apreciável, em geral, a partir de 500oC com a ocorrência de recristalização descontínua. Acima de 700oC, o crescimento normal de grão passa a ser o principal mecanismo de engrossamento microestrutural. Efeitos de orientação importantes foram observados no bicristal nos estados encruado e recozido.
Título en inglés
Processing and microstructural characterization of niobium deformed by equal channel angular extrusion
Palabras clave en inglés
EBSD
ECAE
Niobium
Recrystallization
Severe plastic deformation
Texture
Resumen en inglés
High-purity niobium single crystals, bicrystals and polycrystals were cut out from longitudinal sections of ingots processed by electron beam melting. Samples were deformed by Equal Angular Channel Extrusion (ECAE) at room temperature up to 8 passes, using the route Bc with a die angle  = 90o. Samples were characterized in terms of their microstructural evolution and deformation textures. Microstructural characterization was performed using optical, scanning electron, and transmission electron microscopies, as well as electron-backscatter diffraction measurements (EBSD) to determine both microtexture and mesotexture. Vickers microhardness testing was performed to follow hardening and softening behaviors in the samples. Another single crystal was deformed by 1 pass in an interrupted ECAE experiment using a die angle  = 120o to follow the changes in texture through the extrusion channel. Texture was determined by X ray diffraction and compared with those reported in the literature for deformed bcc materials and also with those predicted using the viscoplastic self-consistent model (VPSC). A comparative study in a larger scale (single and polycrystals) was also performed. It was observed that there is a significant refinement of the microstructure after 8 passes. The average spacing between high angle boundaries perpendicular to extrusion direction was close in the two cases (500 nm), larger than observed in the single crystal deformed in a smaller scale (440 nm). Results also show that ultrafine grains of the deformed polycrystal are more equiaxial compared to those found in the deformed single crystal. Samples were annealed to evaluate their behavior regarding microstructural coarsening. Results show that coarsening becomes noticeable at temperatures higher than 500oC by means of discontinuous recrystallization. Above 700oC, normal grain growth becomes the main microstructure coarsening mechanism. Important orientation effects were observed in the bicrystal in both deformed and annealed states.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMT09003.pdf (19.40 Mbytes)
Fecha de Publicación
2013-08-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.