Doctoral Thesis
DOI
10.11606/T.97.2016.tde-25022016-095201
Document
Author
Full name
Aline Corecha Santos
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Lorena, 2015
Supervisor
Committee
Ribeiro, Sebastiao (President)
Barboza, Miguel Justino Ribeiro
Genova, Luís Antonio
Piorino Neto, Francisco
Strecker, Kurt
Title in Portuguese
Sinterização e caracterização mecânica e microestrutural de cerâmicas de SiC aditivadas com misturas de AIN/Dy2O3 e AIN/Yb2O3
Keywords in Portuguese
Carbeto de silício
Óxido de terras raras
Resistência à flexão
Sinterização
Tenacidade à fratura
Abstract in Portuguese
A obtenção de cerâmicas de SiC pela sinterização com a presença de aditivos que promovam a formação de uma fase líquida (SFL) durante o processo tem sido uma forma adequada para garantir a menor temperatura de sinterização. Pelo fato de o SiC ser frágil, a busca por melhores propriedades mecânicas e avaliação correta das mesmas, para ser aplicado em ambientes agressivos, é contínua. Com base nisso, na primeira etapa, foram estudados, quanto à molhabilidade sobre o SiC, os sistemas AlN/Re2O3 (Re = Dy, Yb) para serem utilizados como aditivos. Os ângulos de contato medidos foram menores que 10° e considerados adequados para a SFL. O SiC sinterizado com esses aditivos permitiu produzir microestruturas diferentes com o aumento da temperatura. Na segunda etapa, foram sinterizadas amostras na forma de pastilhas em várias temperaturas, cujas condições que apresentaram os melhores resultados de massa específica real e densidade relativa foram tomadas como referência para a sinterização na forma de barras prismáticas. Na terceira etapa, essas amostras foram avaliadas quanto à sua tenacidade à fratura (KIC) pelo método da barra entalhada em V, dureza e resistência à flexão. O comportamento de KIC foi avaliado em função da profundidade e raio de curvatura dos entalhes. Os valores variaram entre 2,59 e 3,64 MPam1/2. Verificou-se que os valores de KIC confiáveis foram aqueles encontrados com pequeno raio de curvatura na ponta do entalhe. Quando o raio foi grande, o mesmo não manteve a singularidade da raiz quadrada da ponta do entalhe, e forneceu valores de KIC superestimados. Foram realizados testes para determinar KIC em ar atmosférico e em água, cujos resultados foram menores em água que em ar, com queda entre 2,56 e 11,26%. A maior resistência sob flexão determinada em 4 pontos foi de 482 MPa. Observou-se correlação direta do tamanho dos grãos nos valores de KIC, dureza e módulo de ruptura das cerâmicas de SiC.
Title in English
Sintering, mechanical and microstructural characterization of SiC ceramics with AlN/Dy2O3 and AlN/Yb2O3 additives
Keywords in English
Flexural strength
Fracture toughness
Rare earth oxide
Silicon carbide
Sintering
Abstract in English
Obtaining SiC ceramics by sintering in the presence of additives that promote a liquid phase formation (LPS) during the process has been a proper manner to ensure the lowest sintering temperature. Because SiC is brittle, an ongoing search for better mechanical properties and proper evaluation of these properties for application in aggressive environments maintained. Thus, in the first stage we studied AlN/Re2O3 systems (Re = Dy, Yb), as to their wettability on SiC, for use as additives. The measured contact angles were smaller than 10° and considered suitable for the LPS. The sintered SiC with these additives allowed the production of different microstructures with the increase in temperature. In the second stage, pellet-shaped samples were sintered at various temperatures, and the conditions showing the best density results were taken as reference for sintering prism-shaped bars. In the third stage, these samples were evaluated for toughness (KIC) by single edge V-notched beam method, hardness, and flexural strength. The behavior of KIC was assessed for notch depth and notch radius of curvature. Values ranged between 2.59 and 3.64 MPa/m1/2. The reliable values of KIC were those found with small radius of curvature at the notch tip. When the radius was large, it did not maintain the singularity of the square root of notch tip and provided overestimated KIC values. Tests were performed to determine KIC in atmospheric air and water, and results were lower in water than in air, dropping between 2.56 and 11.26%. The greatest strength under the 4-point bending test was 482 MPa. We observed a direct correlation of grains size in KIC values, hardness and bending strength of SiC ceramics.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
EMT15007_C.pdf (17.13 Mbytes)
Publishing Date
2016-02-25
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2022. All rights reserved.