Mémoire de Maîtrise
DOI
10.11606/D.97.2011.tde-23082013-105827
Document
Auteur
Nom complet
Paulo Roberto Godoy Patrocinio
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2011
Directeur
Jury
Sandim, Hugo Ricardo Zschommler (Président)
Coelho, Gilberto Carvalho
Lins, Jefferson Fabrício Cardoso
Titre en portugais
Caracterização da textura e do orelhamento ("earing"") da liga AA3104 após a redução a frio
Mots-clés en portugais
Alumínio
Laminação
Latas de bebidas
Liga AA3104
Textura
Resumé en portugais
A liga de alumínio AA3104 é utilizada na manufatura de componentes obtidos via estampagem profunda e estiramento, como corpo de latas de bebidas. O presente trabalho visa relatar as principais alterações microestruturais e texturais da liga AA3104 em diferentes condições de deformação a frio. As amostras investigadas foram obtidas por meio de laminação a quente nas espessuras de 1,80 e 2,25 mm. O material A com espessura de 1,80 mm foi laminado duas vezes a frio com reduções de 64% e 59%. Já o material B com espessura de 2,25 mm foi laminado três vezes a frio com reduções de 55%, 52% e 51%. Após cada redução a frio foram retiradas amostras para as caracterizações. A espessura final nos dois materiais foi de 260 ?m. A caracterização microestrutural foi realizada por meio de microscopia ótica convencional e microscopia eletrônica de varredura. A textura de recristalização foi obtida por meio de difração de raios X. Foram realizados ensaios mecânicos para determinar a microdureza e limites de resistência e escoamento das amostras analisadas, além do ensaio de embutimento das amostras para a caracterização do orelhamento. Os melhores resultados de orelhamento foram obtidos no material A e os maiores valores de tensão de escoamento, resistência a tração e microdureza foram observadas no material B. Também foram retiradas amostras de latas de bebidas após a estampagem e após a estampagem e recozimento para a caracterização microestrutural. A ênfase desta Dissertação visa avaliar a influência da quantidade de deformação a frio aplicada em chapas recristalizadas provenientes da laminação a quente na textura cristalográfica e no comportamento das chapas durante o ensaio de orelhamento.
Titre en anglais
Texture and earing characterization of AA3104 alloy after cold rolling
Mots-clés en anglais
Alloy AA3104
Aluminum
Beverage can
Rolling
Texture
Resumé en anglais
The aluminum alloy AA3104 is widely used in the manufacture of components obtained by deep drawing and ironing, as the body of beverage cans. The present work describes the main microstructural and textural changes of AA3104 alloy following different cold rolling schedules. The samples were obtained after hot rolling, with thicknesses of 1.80 and 2.25 mm. Material A (1.80 mm) was cold rolled in two steps with reductions of 64% and 59%, respectively. Material B (2.25 mm) was cold rolled in three steps with reductions of 55%, 52% and 51% respectively. After each cold reduction samples were removed for microstructural characterization. The final thickness of the two materials was 260 ?m. The microstructural characterization was performed using conventional light optical and scanning electron microscopy. The recrystallization texture was determined by X-ray diffraction measurements. Mechanical tests were carried out to determine the Vickers microhardness as well as yield and tensile strengths. Deep drawing tests were performed for earing characterization. The best results of earing were obtained in material B. The highest yield and tensile strengths were observed in material A. Samples of commercial beverage cans were taken after deep drawing and annealing (drying) for microstructural characterization. The emphasis of this study is to evaluate the influence of the cold deformation in hot-rolled sheets regarding crystallographic texture evolution and corresponding behavior during earing tests.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EMD11011.pdf (4.59 Mbytes)
Date de Publication
2013-08-23
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.