Dissertação de Mestrado
DOI
10.11606/D.97.2011.tde-22082013-172245
Documento
Autor
Nome completo
Maxwell Pereira Cangani
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Lorena, 2011
Orientador
Banca examinadora
Rodrigues Junior, Durval (Presidente)
Hein, Luis Rogério de Oliveira
Santos, Claudinei dos
Título em português
Caracterização microestrutural de ZrO2 estabilizada com Y2O3 sinterizada a partir de pós nanocristalinos
Palavras-chave em português
análise digital de imagens
microestrutura
pós nanocristalinos
sinterização
ZrO2
Resumo em português
Materiais cerâmicos obtidos a partir de pós nanocristalinos permitem a obtenção de excelentes propriedades após sinterização, devido à possibilidade de redução da temperatura final de sinterização com conseqüente refinamento microestrutural e excelente densificação. Nesse contexto, a zircônia tetragonal (ZrO2 (t)) tem um importante papel, pois suas características intrínsecas, tais como a transformação martensítica (ZrO2 (t-m)), permitem o desenvolvimento de excelentes propriedades, destacando-se a elevada tenacidade à fratura e resistência a flexão, tornando-a um material diferenciado visando aplicações nobres onde propriedades mecânicas e confiabilidade sejam pré-requisitos. Visando otimizar estas aplicações, se faz necessário conhecer as correlações entre as propriedades mecânicas e a microestrutura. Sendo assim, é de extrema importância promover a revelação microestrutural desses materiais, de forma padronizada e com representatividade estatística, o que exige cuidados nas técnicas de preparação ceramográfica. Nesse trabalho pretende-se caracterizar microestruturalmente cerâmicas a base de ZrO2(Y2O3) nanométrica, visando estudar os efeitos da temperatura e do tempo de sinterização na cinética de crescimento de grão. Foi definida uma rota de preparação e análise ceramográfica propondo seqüência de lixas e panos de polimento, assim como cargas e tempos em cada etapa. As amostras foram atacadas termicamente e micrografias foram obtidas. As micrografias foram processadas por rotinas de análise digital de imagens, visando definir padronizações para determinação de parâmetros microestruturais de interesse, tais como distribuição de tamanhos de grãos, densidade de grãos por unidade de área, razão de aspecto, etc. Foi estudado o efeito das condições de sinterização (temperatura final e tempo de isoterma) no crescimento de grãos.
Título em inglês
Microstructural characterization of ZrO2 stabilized with Y2O3 sinterized from nanocrystalline powders
Palavras-chave em inglês
digital image analysis
microstructure
nanocrystalline powders
sintering
ZrO2
Resumo em inglês
Ceramic materials obtained from nanocrystalline powders enable the obtaining of excellent properties after sintering, due to the possibility of reducing the final sintering temperature with consequent microstructural refinement and excellent densification. In this context, tetragonal zirconia (ZrO2 (t)) has an important role, since their intrinsic characteristics, such as the martensitic transformation (ZrO2 (t-m)), allow the development of excellent properties, highlighting the high tenacity to fracture and resistance to bending, making it a differentiated material aiming noble applications where mechanical properties and reliability are prerequirements. In order to optimize these applications, it is necessary to know the correlations between the mechanical properties and microstructure. Thus, it is extremely important to promote the microstructural disclosure of these materials, in a standardized manner and with statistical representativeness, which requires care with the ceramographic preparation techniques. This work aims to microstructurally characterize ceramics based on nanometric ZrO2(Y2O3), looking for the study of the effects of the sintering temperature and time on the graingrowth kinetics. It was defined a route for ceramographic preparation and analysis proposing a sequence of sandpapers and polishing cloths, as well as loads and times at each stage. The samples were thermally etched and micrographs were obtained. The micrographs were processed through routines of digital image analysis, aiming the definition of standards for the determination of microstructural parameters of interest, such as distribution of grain sizes, density of grains per unit of area, aspect ration, and others. It was studied the effects of the sintering conditions (final temperature and time of isotherm) on the grain growth.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
EMD11010.pdf (6.42 Mbytes)
Data de Publicação
2013-08-22
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.