Mémoire de Maîtrise
DOI
10.11606/D.97.2008.tde-20082013-155232
Document
Auteur
Nom complet
José Mauro Moraes Junior
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2008
Directeur
Jury
Nunes, Carlos Angelo (Président)
Guimarães, Valdir Alves
Barboza, Miguel Justino Ribeiro
Titre en portugais
Influência do tratamento térmico de alívio de tensões pós-soldagem na microestrutura e comportamento mecânico de soldas produzidas com arame tubular rutílico
Mots-clés en portugais
Alívio de tensões
Arame tubular rutílico
Microestrutura
Tenacidade ao impacto
Resumé en portugais
O objetivo desta Dissertação foi analisar o efeito do tratamento térmico de alívio de tensões pós-soldagem sobre a microestrutura e comportamento mecânico de soldas produzidas com arame tubular rutílico AWS E-81T1 Ni1. Foi soldada uma junta com 60 mm de espessura, na posição vertical e progressão ascendente. Esta junta foi dividida em três partes, sendo uma mantida como soldada e as outras duas tratadas termicamente por 6 horas em diferentes temperaturas, 585 °C e 650 °C. Avaliou-se o efeito do tratamento térmico sobre as propriedades mecânicas por meio de ensaio de dureza, tração e impacto Charpy-V. A caracterização microestrutural foi realizada por microscopia óptica e microscopia eletrônica de varredura. As observações experimentais mostraram uma diminuição da tenacidade ao impacto no material tratado termicamente, com uma tendência para uma queda maior com o aumento da temperatura do tratamento térmico. Este comportamento pode ser atribuído principalmente à precipitação e crescimento de carbonetos. Não foi observada a presença de mecanismos de fratura intergranular. Provavelmente o metal de solda estudado não possuía nível de impurezas suficiente para a ativação deste mecanismo.
Titre en anglais
Influence of Postweld Heat Treatment in Microstructure and Mechanical Behavior of Weld Obtained by Rutile Flux-Cored Wire
Mots-clés en anglais
Impact toughness
Microstructure
Rutile flux-cored wire
Stress relief
Resumé en anglais
The objective of this Dissertation was to analyze the effect of postweld heat treatment on microstructure and mechanical behavior of welds obtained by flux cored wire AWS E-81T1 Ni1. It was welded a joint with 60 mm thickness, on vertical position and ascendant progress. This joint was divided in three parts, one maintained as welded and two others heat treated for 6 hours on different temperatures, 585 °C and 650 °C. The effect of the heat treatment on mechanical properties was evaluated by means of hardness, tensile and impact Charpy-V tests. The characterization of the microstructure was undertaken utilizing optical and scanning electron microscopy. The experimental results revealed a decrease of impact toughness in heat treated material, with a tendency to a low impact toughness for high heat treatment temperature. This behavior may principally be attributed to an increase precipitation and growth of carbides. No intergranular fracture mechanism was observed. Probably the level of impurities in the weld metal studied was not high enough to provoke such phenomena.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EMD08006.pdf (14.13 Mbytes)
Date de Publication
2013-08-20
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.