Disertación de Maestría
DOI
10.11606/D.97.2016.tde-13092016-110132
Documento
Autor
Nombre completo
André Navarro de Miranda
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2016
Director
Tribunal
Vieira, Ricardo (Presidente)
Cruz, Gilberto Marques da
Ribeiro, Sebastiao
Título en portugués
Síntese e caracterização de óxidos mistos de cobalto, manganês e alumínio para decomposição catalítica de H2O2 70% e geração de vapor
Palabras clave en portugués
Catalisador
Espinélios
Geração de vapor
Óxidos mistos
Peróxido de hidrogênio
Resumen en portugués
Este trabalho teve como objetivo o desenvolvimento de catalisadores mássicos à base de óxidos mistos de cobalto, manganês e alumínio, para a decomposição de peróxido de hidrogênio comercial, 70% em massa, e consequente geração de vapor d'água. A síntese dos materiais foi realizada por coprecipitação em meio básico. Durante a reação foram sistematicamente estudados o pH do meio, a concentração inicial de carbonato, a velocidade de agitação, o tempo de envelhecimento, a influência da lavagem do precitado, o diâmetro médio das partículas e a temperatura e tempo de tratamento térmico. Os materiais foram caracterizados quanto as fases presentes, porcentagem mássica, massa específica, área específica, resistência mecânica e atividade catalítica, visando correlacionar suas propriedades físico-químicas com sua atividade na decomposição catalítica do peróxido de hidrogênio. Finalmente, os materiais que apresentaram melhor resistência mecânica e atividade catalítica foram testados em um sistema gerador de vapor. O melhor catalisador apresentou alta resistência mecânica, baixo tempo de indução e se mostrou ativo em testes de longa duração, possibilitando ao sistema alcançar temperaturas próximas à de decomposição adiabática do H2O2 70% em massa.
Título en inglés
Synthesis and characterization of mixed oxides of cobalt, manganese and aluminum for catalytic decomposition of H2O2 70% and steam generation
Palabras clave en inglés
Catalysts
Hydrogen Peroxide
Mixed Oxides
Spinels
Steam generation
Resumen en inglés
This work aimed to develop catalysts based on mixed oxides of cobalt, manganese and aluminum for the decomposition of commercial hydrogen peroxide, 70% p, inducing steam generation. The materials were synthesized by coprecipitation under alkaline condition. During reaction, were systematically studied the pH of the solution, the initial concentration of carbonate, the stirring speed, the aging time, the precipitate washing, the average particle diameter, the temperature and time of thermal treatment. The materials were characterized to determine the present phases, mass concentration, density, surface area, mechanical strength and catalytic activity, aiming to correlate their physicochemical properties with its activity on hydrogen peroxide catalytic decomposition. Once the best parameters were set, the best catalysts were tested in a steam generating system. The best catalyst have presented high mechanical strength, low induction time and proved to be active in long-term tests, enabling the system to reach temperatures close to the adiabatic decomposition of the H2O2 70% wt.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD16003_C.pdf (2.88 Mbytes)
Fecha de Publicación
2016-09-13
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.