Dissertação de Mestrado
DOI
10.11606/D.97.2016.tde-06072016-151412
Documento
Autor
Nome completo
Alexandra de Almeida Diego
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Lorena, 2016
Orientador
Banca examinadora
Vernilli Junior, Fernando (Presidente)
Coelho, Gilberto Carvalho
Silva, Sidiney Nascimento
Título em português
Influência da substituição de matérias primas nas propriedades dos fluxantes para lingotamento contínuo de aços médio carbono
Palavras-chave em português
fluxante
lingotamento contínuo
propriedades físico-químicas
Resumo em português
O fluxante é uma escória sintética que influencia na qualidade superficial do aço e na estabilidade do processo de lingotamento contínuo. Este produto é aplicado diretamente sobre o aço líquido na região do molde de cobre refrigerado a água e atua diretamente no resfriamento primário do aço. O fluxante tem as propriedades físico-químicas adaptadas para cada tipo de aço e também para as condições de lingotamento. Na superfície do aço líquido, o fluxante funde e forma uma poça líquida, atuando como isolante térmico, protegendo o aço da reoxidação e absorvendo inclusões principalmente de Al2O3. A poça líquida escoa, lubrificando e controlando a transferência de calor na interface entre o molde e a pele de aço em solidificação. O problema de qualidade superficial do aço, quando relacionado ao fluxante, se resume a alarmes de colamento, trincas de quina, marcas de oscilação profundas e trincas longitudinais, sendo este último um problema particular do aço médio carbono. Neste trabalho, foram analisados diferentes fluxantes baseados inicialmente no fluxante comercial aplicado no lingotamento contínuo de placas de aço médio carbono. Todos os fluxantes foram desenvolvidos com composições químicas similares. O objetivo foi avaliar o impacto da substituição de fontes de matérias-primas em diferentes composições de modo a avaliar as propriedades físico-químicas com base no fluxante comercial de referência. Como resultado, de todas as propriedades físico-químicas, foi a temperatura de cristalização que sofreu a alteração mais significativa.
Título em inglês
The Influence of the replacement of raw materials on the properties of mold fluxes for continuous casting of medium carbon steel
Palavras-chave em inglês
continuous casting
mould flux
physicochemical properties
Resumo em inglês
The mould flux is a synthetic slag which influences the quality of steel surface and also the stability of the continuous casting process. This product is applied in direct contact with the surface of liquid steel in the region of the water cooled cupper mold and acts directly on the primary cooling of steel. The mould flux has the physical and chemical properties adapted for each type of steel as weel as casting conditions. On the surface of liquid steel, the mould flux melts and forms the liquid pool, working as an insulator, protecting the steel against reoxidation and also absorbing mainly Al2O3 inclusions. The liquid pool flows, lubricating and controlling the heat transfer in the interface between the mold and the steel shell during solidification. The surface quality issues when related with mould flux can cause alarms of breakout, corner cracks, deep oscillation marks, longitudinal cracks that is a particular problem in medium carbon steel grade. In this study, different mould fluxes were investigated and compared to a commercial mould flux applied to the continuous casting of slabs in the medium carbon steel grade. All mould fluxes were developed with a similar chemical composition. The main goal was to evaluate the impact of changing raw material sources on the physicochemical properties of the different mould fluxes and the results was compared with a commercial standard mould flux. As result, variations in the crystallization temperatures were observed more than others properties analyzed.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
EMD15014_C.pdf (3.36 Mbytes)
Data de Publicação
2016-07-06
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.