Tesis Doctoral
DOI
https://doi.org/10.11606/T.97.2019.tde-05082021-164700
Documento
Autor
Nombre completo
Davison Ramos de Almeida Junior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2019
Director
Tribunal
Sandim, Hugo Ricardo Zschommler (Presidente)
Fonseca, Gláucio Soares da
Rios, Paulo Rangel
Silva, André Luiz Vasconcellos da Costa e
Título en portugués
Crescimento anormal de grão em fios finos de ferro comercialmente puro
Palabras clave en portugués
Crescimento anormal de grão
EBSD
Ferro de pureza comercial
Fios
Trefilação a frio
Resumen en portugués
O crescimento anormal de grão em fio de metais com estrutura ccc foi bastante estudado no início do século XX devido ao desenvolvimento da indústria de filamentos para lâmpadas incandescentes. A presente Tese de Doutorado estuda o crescimento anormal de grão num fio de ferro de pureza comercial. A revisão bibliográfica apresenta os aspectos físicos mais relevantes do fenômeno, bem como características para o caso de fios trefilados de metais com estrutura cúbica de corpo centrado. A análise experimental baseia-se nos resultados obtidos por microscopia ótica, eletrônica de varredura, eletrônica de transmissão, difração de elétrons retroespalhados e tomografia de sonda atômica. Os resultados do material na condição "como recebido" mostram a existência de heterogeneidades microestruturais importantes ao longo da direção radial do fio no estado deformado e que explicam as características heterogêneas na recristalização primária e no crescimento de grão. A recristalização primária resulta em heterogeneidades de tamanho de grão. O posterior recozimento em 850°C mostra um ligeiro crescimento normal de grão para tempos de recozimento inferiores a 4 h que ocorre de forma mais intensa na região central do fio. Os grãos anormais das amostras recozidas por mais de 4 h aparecem no centro e possuem orientação preferencial da fibra // WD (onde WD é a direção de trefilação). A distribuição dos precipitados é heterogênea devido à interação entre amostra e atmosfera, o que garante baixa mobilidade para os contornos próximos à superfície livre mesmo após prolongado recozimento. Os resultados mostram que a ocorrência de crescimento normal é um fator necessário para o surgimento de grãos anormais. Esta interpretação possui fundamentos topológicos e apresenta maior aderência aos resultados experimentais do que outros modelos teóricos reportados na literatura.
Título en inglés
Abnormal grain growth in thin wires of commercially-pure iron
Palabras clave en inglés
Abnormal Grain Growth
Cold drawing
Commercially-pure iron
EBSD
Wires
Resumen en inglés
Abnormal grain growth in wires of bcc metals has been studied extensively since the beginning of the XXth Century due to the development of tungsten filaments for bulb lamps. The present thesis aims to study the abnormal grain growth in commercially-pure iron wires. The revision of literature presents the physical aspects most relevant for the phenomenon, as well as the main features occurring in wires of bcc metals during their annealing. The experimental analysis was performed by using light optical microscopy, scanning and transmission electron microscopy, electron backscatter diffraction and atom probe tomography. The results of the sample in the as-received condition show the occurrence of inhomogeneities of the deformation microstructure along the radial direction, which explains the inhomogeneous features noticed in primary recrystallization as well as in grain growth. The recrystallized samples show an inhomogeneous grain size distribution along the radial direction. Isothermal annealing at 850°C shows the occurrence of moderate normal grain growth up to 4 h. For longer times, abnormal grain growth is noticed. Normal grain growth is more effective at the center. Abnormal grains appear at the center and present preferential orientation // WD, where WD is the wiredrawing direction. The particle size distribution is heterogeneously distributed along the radial direction and it is strongly dependent on the interaction between the wire and the annealing atmosphere. This feature is effective to hinder the boundary movement close to the surface. Prior normal grain growth is a key factor to trigger abnormal grain growth. This interpretation is based on topological features and presents better adherence to experimental results when compared with other theoretical models reported in the literature.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMT19001_O.pdf (6.89 Mbytes)
Fecha de Publicación
2021-08-05
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.