Mémoire de Maîtrise
DOI
10.11606/D.97.2015.tde-05082015-154141
Document
Auteur
Nom complet
Matheus Martini
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2015
Directeur
Jury
Vernilli Junior, Fernando (Président)
Justus, Sérgio Murilo
Silva, Sidiney Nascimento
Titre en portugais
Avaliação do potencial de expansão de agregados siderúrgicos através da Difratometria de Raios X e Método de Rietveld
Mots-clés en portugais
difratometria de raios X
escória
expansibilidade
método de Rietveld
Siderurgia
Resumé en portugais
A escória de aciaria LD é um coproduto originado do refino do ferro gusa em aço e da metalurgia secundária, sendo gerado, em média, uma quantidade de aproximadamente 120 kg/t de aço produzido. Assim como as escórias de alto-forno, que são utilizadas como matéria-prima para a fabricação do cimento, as escórias de aciaria LD, após beneficiamento (chamadas de agregados siderúrgicos), possuem diversas aplicações, tais como: artigos de concreto, diques marítimos, tratamentos de efluentes, lastro ferroviário, base e sub-base para pavimentos de rodovia, corretivo de solos, entre outros. Entretanto, este material possui compostos (CaO e MgO quando livres, Fe0, FeO e mCaO.nSiO2) que sofrem reações quando exposto ao ambiente, provocando expansão e desintegração dos materiais onde é aplicado, sendo necessária a estocagem em pátios para cura ou envelhecimento e consequente minimização da expansão. Atingido um determinado tempo de envelhecimento, o agregado é avaliado sob o ponto de vista do potencial de expansão para que, a partir dos resultados obtidos, seja ainda mantido sob cura ou destinado à sua aplicação. Os métodos mais comuns que avaliam a expansão de escórias de aciaria são o PTM-130/78, JIS A 5015/92 e o ASTM D4792/00. No Brasil, atualmente, o ensaio PTM-130 é o mais utilizado pelo Departamento de Estradas de Rodagem, entretanto o método leva 14 dias para obtenção dos resultados, que em geral são pouco detalhados sobre o comportamento da escória. Desta forma, o presente trabalho buscou correlacionar o método de avaliação do potencial de expansão volumétrica da escória de aciaria LD com a concentração de determinados compostos, quantificados através da difratometria de raios X em pós e o método de Rietveld, respectivamente. Buscou-se, também, compreender a influência dos diferentes compostos sobre a expansibilidade.
Titre en anglais
Evaluation of potential for expansion of steel slag aggregates through X-ray diffractometry and Rietveld Method
Mots-clés en anglais
BOF slag
expansion
Rietveld method
Steel industry
x-ray diffractometry
Resumé en anglais
BOF slag is a byproduct originated from the hot metal refining to steel and its subsequent types of secondary metallurgy processes, being generated, on average, an amount about 120 kg/t of steel. Similar to blast furnace slag which is used as raw material for the manufacturing of cement, BOF slag, after treatment (so-called of steel slag aggregates), has many applications such as: concrete components, marine docks, effluent treatment, ballast, road and highways base, correction of soil, among others. However, BOF slag is composed by chemical products (such as free CaO and MgO, Fe0, FeO and mCaO.nSiO2) which suffer expansive reactions when exposed to the atmosphere, causing expansion and disintegration of the materials where it is applied. Therefore, it is required some temporary storage for curing or aging to minimize the volumetric instability that is evaluated trough the potential of expansion. Depending on the volumetric expansion results, steel slag aggregates may be approved or disapproved according to a specified limit that will allow to be used or not. The most common methods to evaluate the expansion of BOF slags are the PTM-130/78, JIS A 5015/92 and ASTM D4792:2013. In Brazil, PTM-130 test is currently the most used by the department of highways. This method spends 14 days to obtain the result that generally shows few details about the behavior. Thus, the present study has the purpose of correlating the traditional method of evaluation with the one of X-ray diffraction in powders associated to the Rietveld Method. Another goal is to understand the influence of different compounds on expansion.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EMD15001_C.pdf (12.58 Mbytes)
Date de Publication
2015-08-05
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.