Tesis Doctoral
DOI
10.11606/T.97.2011.tde-03102012-114712
Documento
Autor
Nombre completo
Juliana Kelmy Macario de Faria Daguano
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2011
Director
Tribunal
Santos, Claudinei dos (Presidente)
Melo, Francisco Cristovão Lourenço de
Ortega, Fernando dos Santos
Ribeiro, Sebastiao
Schneider, Sandra Giacomin
Título en portugués
Biovidros e vitrocerâmicos bioativos do sistema 3Ca0.P205-Si02-MgO para aplicações biomédicas: processamento e caracterizações estruturais mecânicas e biológicas
Palabras clave en portugués
Biomateriais
Biovidro
Cristalização
Propriedades Mecânicas
Testes in vitro
Resumen en portugués
Este trabalho apresenta o desenvolvimento e a caracterização de biovidros e vitrocerâmicos bioativos do sistema 3CaO.P2O5-SiO2-MgO, com índices de cristalinidade variados, visando o uso destes materiais em implantes estruturais ósseos. Amostras de composição nominal (% em peso) 57,75% CaO.P2O5 - 30% SiO2 - 17,25% MgO foram obtidas por fusão, e posteriormente, tratamentos térmicos foram realizados para a cristalização parcial dos vitrocerâmicos em temperaturas entre 700 ºC e 1100 ºC, com tempos diversos de até 480 minutos. Esses materiais foram caracterizados quanto ao seu comportamento térmico, quanto às fases cristalinas presentes e à microestrutura. Os resultados mostram que o vidro base apresenta separação de fases amorfas e os vitrocerâmicos apresentam como fase cristalina majoritária a fase whitlockite, podendo ser encontrada também a fase diopsídio, em tratamentos térmicos acima de 1050 °C. As propriedades mecânicas de dureza, tenacidade à fratura, módulo de fratura por ensaio de flexão e módulo elástico dinâmico foram determinadas. Todas as propriedades foram avaliadas em função do grau de cristalinidade do material, mostrando que a microestrutura e a fração cristalizada, bem como as diferentes fases cristalinas presentes, influenciam os resultados obtidos. O ganho máximo nas propriedades mecânicas ocorre em tratamentos térmicos a 975 °C, sendo atingidos valores próximos a 6,2 GPa, 1,7 MPa.m1/2 e 120 MPa para a dureza, a tenacidade à fratura e o módulo de fratura, respectivamente, em comparação aos valores de 4,8 GPa, 1,1 MPa.m1/2, 71 MPa dos vidros nucleados, o que indica aumento da ordem de 30% na dureza, 55% na tenacidade e 70% na resistência à fratura. Para o teste in vitro de citotoxicidade foram utilizadas células CHO como meio de cultura. Para os testes de bioatividade, as trocas iônicas entre os materiais e a solução acelular SBF ressaltam as diferenças em termos de reatividade química, sendo o efeito da cristalização de biovidros na formação da HCA observado por FTIR. Todas as amostras não apresentaram caráter citotóxico e o vitrocerâmico tratado a 775 °C mostrou ser o material mais bioativo, com início de formação da HCA em período de 24 h. Assim, os resultados obtidos indicam que o vidro e os vitrocerâmicos do sistema 3CaO.P2O5-SiO2-MgO são promissores candidatos ao uso como implantes ósseos, com distintas características e propriedades.
Título en inglés
Biglasses and bioactive glass-ceramics based on 3CaO.P2O5-SiO2-MgO-system for biomedical applications: processing, and structural, mechanical and biological characterization
Palabras clave en inglés
Bioglass
Biomaterials
Crystallization
In vitro tests
Mechanical Properties
Resumen en inglés
The current work presents the development and characterization of bioglass and bioactive glass-ceramic based on 3CaO.P2O5-SiO2-MgO-system, with different crystallization degrees, in order to use these materials in bone restorations. Samples of nominal composition (wt%) 57.75% CaO.P2O5-30% SiO2-17.25% MgO were obtained by melting and after heat-treated to partial crystallization of glass-ceramic at temperatures between 700 ºC and 1100 °C , with times up to 480 minutes. These materials were characterized by thermal analysis, X-Ray diffraction and scanning electron microscopy. The results showed amorphous phase separation in glasses. In glass-ceramics, it was identified whitlockite as major crystal phase, and diopside phase above 1050 °C. Hardness, fracture toughness, bending strength and elastic modulii of the samples were evaluated. These mechanical properties were evaluated according to the matrix crystallinity degree. The microstructure and the crystallization degree must be influencing the mechanical properties results. The optimized properties were observed in samples crystallized at 975 °C, with values near to 6.2 GPa, 1.7 MPa.m1/2 and 120 MPa for hardness, fracture toughness and bending strength, respectively, in comparison to 4.8 GPa, 1.1 MPa.m1/2 and 71 MPa presented by nucleated glasses at 700 °C, which indicates increases of 30% in hardness, 55% in fracture toughness and 70% in bending strength. In the cytotoxicity test, the culture medium was CHO cells. Ionic exchanges with the SBF-K9 acellular solution during the in vitro bioactivity tests highlight the differences in terms of chemical reactivity between the glass and the glassceramics. The effect of crystallinity on the rates of hydroxycarbonate apatite (HCA) formation was followed by FTIR. All samples were considered not cytotoxic. The glassceramic obtained at 775 °C presented the most interesting result, because onset for HCA formation is about 24 hours.The results obtained indicate that glasses and glass-ceramics of the 3CaO.P2O5-SiO2-MgO system are promissory candidates to be used as bonegraft implants.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMT11001_pt1.pdf (2.79 Mbytes)
EMT11001_pt2.pdf (5.75 Mbytes)
EMT11001_pt3.pdf (5.23 Mbytes)
EMT11001_pt4.pdf (10.27 Mbytes)
Fecha de Publicación
2012-10-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.