Doctoral Thesis
DOI
10.11606/T.97.2010.tde-20082013-150509
Document
Author
Full name
Simone de Fátima Medeiros
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Lorena, 2010
Supervisor
Committee
Santos, Amilton Martins dos (President)
Barboza, Jayne Carlos de Souza
Elaissari, Abdelhamid
Fessi, Hatem
Muniz, Edvani Curti
Title in Portuguese
Obtenção de nanopartículas magnéticas sensíveis a estímulos para aplicações biomédicas
Keywords in Portuguese
Aplicações biomédicas
Cinética de polimerização
LCST
N-vinilcaprolactama
Nanopartículas magnéticas
Polimerização em miniemulsão
Abstract in Portuguese
Partículas poliméricas com propriedades magnéticas podem ser utilizadas tanto em aplicações terapêuticas in vivo, como agentes de liberação controlada de princípios ativos, ex vivo, na extração de células cancerígenas do organismo, ou ainda in vitro, em diagnósticos. A necessidade de materiais inteligentes e biocompatíveis, como agentes de encapsulação destas partículas magnéticas, leva ao uso de polímeros sensíveis a estímulos. Em aplicações terapêuticas, esta tecnologia é baseada na localização das partículas através da aplicação de um campo magnético e na concentração da droga na área de interesse. Esta etapa é seguida pela liberação da droga, utilizando-se as propriedades sensíveis dos polímeros. Dessa forma, este trabalho de tese se dedica ao estudo da obtenção de nanopartículas constituídas de uma matriz polimérica sensível a estímulos e de partículas de óxido de ferro (?-Fe2O3 e Fe3O4). Inicialmente, nanogéis à base de poli(NVCL-co-AA) foram obtidos através do método de polimerização por precipitação. A Poli(Nvinilcaprolactama) (PNVCL) é um polímero termo-sensível, que possui temperatura crítica inferior de solubilização (LCST) próxima à temperatura fisiológica (35-38 ºC) e é conhecida, ainda, por possuir maior biocompatibilidade, em comparação a outros polímeros do gênero. O poli(ácido acrílico) (PAA), por sua vez, é um polímero que apresenta sensibilidade ao pH. Nesta etapa estudou-se a influência de alguns parâmetros de síntese nos diâmetros de partículas, na polidispersidade e na sensibilidade à temperatura dos nanogéis. A sensibilidade ao pH também foi estudada em função da concentração de ácido acrílico adicionado nas sínteses. Em seguida, realizou-se o estudo da encapsulação de nanopartículas magnéticas complexadas com dextrana em nanogéis de PNVCL, utilizando-se a técnica de polimerização em miniemulsão inversa. Os nanogéis magnéticos sensíveis à temperatura foram caracterizados quanto ao diâmetro de partículas (DP) e distribuição do diâmetro de partículas (DDP), pela técnica de espalhamento de luz. A sensibilidade à temperatura dos nanogéis magnéticos também foi estudada por espalhamento de luz, através de medidas de diâmetro de partículas em diferentes temperaturas. As medidas de magnetização foram obtidas em um magnetômetro de amostra vibrante (MAV). Análises de infra vermelho (FTIR) e de difratometria de raios X revelaram qualitativamente a encapsulação das nanopartículas magnéticas. A eficiência de incorporação das nanopartículas de óxido de ferro foi estudada através de análises termogravimétricas (TGA) e medidas de magnetização. As características morfológicas dos nanogéis magnéticos foram observadas por microscopia eletrônica de transmissão (TEM).
Title in English
Preparation of stimuli-responsive magnetic nanoparticles for biomedical applications
Keywords in English
Biomedical applications
LCST
Magnetic nanoparticles
Miniemulsion polymerization
N-vinylcaprolactam
Polymerization kinetics
Abstract in English
Polymeric particles with magnetic properties can be useful for in vivo therapeutic applications, as agents for controlled drug release, for ex vivo applications, as agents for the extraction of cancer cells, and finally, for the diagnosis in vitro. The search for biocompatible and smart materials as agents for the encapsulation of magnetic particles, leads to the use of stmuli-responsive polymers. In therapeutic applications, this technology is based on the localization and the concentration of the particles containing the drug in the area of interest by applying a magnetic field. This step is followed by the release of the drug, using the sensitive properties of the polymers. In this context, this thesis is devoted to the preparation of nanoparticles constituted by a stimuli-responsive polymer matrix and particles of iron oxide (?-Fe2O3 e Fe3O4). First of all, we performed the synthesis of poly(NVCL-co-AA)-based nanogels using the precipitation polymerization method. Poly(N-vinilcaprolactama) (PNVCL) is a thermo-responsive polymer which presents the lower critical solution temperature (LCST) near the physiological temperature (35-38 °C) and it is well known by its greater biocompatibility, in comparison with other themallysensitive polymers. On the other hand, the poly(acrylic acid) (PAA) is known by its sensibility to changes in the enviromental pH. In this stage, the influence of some synthesis parameters on the particles diameter, polydispersity and themally-sensitive behavior of the nanogels was evaluated. The pH-sensibility behavior was also studied as a function of the AA concentration in the synthesis. As a second step, the study of the incorporation of dextran-coated magnetic nanoparticles in the PNVCL-based nanogels using the inverse miniemulsion polymerization was preformed. The thermo-responsive magnetic nanogels were characterized in terms of particles diameter (PD) and particles size distribution (PSD) using light scattering. The temperature sensitivity of the magnetic nanogels was also studied by light scattering, with measurements of particles diameter as a function of temperature. The magnetization measurements were obtained on a vibrating sample magnetometer (VSM). Analysis of infra-red (FTIR) and X-ray diffraction revealed qualitatively the incorporation of magnetic nanoparticles. The incorporation efficiency of iron oxide nanoparticles was studied by thermo-gravimetric analysis (TGA) and magnetic measurements. The morphological characteristics of the magnetic nanogels were observed by transmission electron microscopy (TEM).
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
EMT10005.pdf (6.23 Mbytes)
Publishing Date
2013-08-20
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.