Tesis Doctoral
DOI
10.11606/T.97.2010.tde-04102012-120438
Documento
Autor
Nombre completo
Mauricio Pinheiro de Oliveira
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2010
Director
Tribunal
Santos, Amilton Martins dos (Presidente)
Barboza, Jayne Carlos de Souza
Giudici, Reinaldo
Lona, Liliane Maria Ferrareso
Oliveira, Pedro Carlos de
Título en portugués
Síntesse de novos estabilizantes poliméricos do tipo poli(álcool vinilico-co-neo decanoato de vinila) para utilização na copolimerização em miniemulsão do acetato de vinila (VAc) com o neo-nonanoato de vinila (VEOVA-9)
Palabras clave en portugués
Acetato de vinila
Adesivos
Poli(álcool vinílico)
Polimerização em miniemulsão
VEOVA-10
VEOVA-9
Resumen en portugués
Devido à importância industrial e tecnológica dos látices estabilizados com poli(álcool vinílico)/PVA e a dificuldade encontrada na etapa de polimerização em emulsão, na presença de monômeros hidrofóbicos e de PVA's com alto grau de hidrólise (>92%), a síntese de novos estabilizantes poliméricos derivados de PVA para utilização em reações de polimerização em emulsão e em miniemulsão se torna muito atraente e desafiadora. O objetivo principal deste trabalho foi sintetizar novos estabilizantes poliméricos do tipo poli(álcool vinílico-co-neodecanoato de vinila)/PVA-VV com alto grau de hidrólise e conseqüentemente com propriedades diferenciadas, para serem utilizados como estabilizantes nas reações de polimerização em emulsão e em miniemulsão do acetato de vinila (VAc) com o neo-nonanoato de vinila (VEOVA-9), visando a obtenção de adesivos com propriedades diferenciadas para colagem de madeiras. Os novos estabilizantes poliméricos foram obtidos em duas etapas: i) copolimerização em solução do VAc com o neo-decanoato de vinila (VEOVA-10); ii) hidrólise alcalina (NaOH/Metanol) do poli(acetato de vinila-coneodecanoato de vinila). As miniemulsões de VAc com VEOVA-9 com diferentes tipos de estabilizantes poliméricos foram preparadas em um homogeneizador de alta pressão do tipo "Manton Gaulin". Foi estudado o efeito dos estabilizantes poliméricos (PVA e PVA-VV) na etapa de emulsificação (diâmetro médio das gotas, polidispersão, estabilidade das miniemulsões) e na copolimerização em emulsão e em miniemulsão do VAc com o VEOVA-9, em processo batelada. O efeito do tipo de iniciador (persulfato de amônio/APS e hidroperóxido de tércio butila/TBHP e peróxido benzoato de tércio butila/TBPB, juntamente com o formaldeído sulfoxilato de sódio/SFS) na cinética da polimerização em miniemulsão do VAc com o VEOVA-9 foi estudado em processo semi-contínuo. A distribuição dos estabilizantes poliméricos (PVA e PVA-VV) entre a fase aquosa e a superfície das partículas de polímero (adsorvido/enxertado) foi determinada e correlacionada com a viscosidade e a estabilidade coloidal dos látices. Látices na condição ideal de cópia (1:1) das gotas de monômero para as partículas de polímero foram obtidos via polimerização em miniemulsão, apresentando propriedades diferenciadas, tais como, menores valores de viscosidade, menor concentração de coágulos e maior estabilidade de estocagem, em comparação com os látices obtidos em emulsão.
Título en inglés
Synthesis of new poly(vinyl alcohol-co-vinyl neodecanoate) based polymeric stabilizers, to be used in the miniemulsion copolymerizatin of vinyl acetate (VAc) with vinyl neononanoate (VEOVA-9).
Palabras clave en inglés
Adhesives
Miniemulsion polymerization
Poly(vinyl alcohol)
VEOVA-10
VEOVA-9
Vinyl acetate
Resumen en inglés
Due to the technological and industrial importance of latexes stabilized with poly(vinyl alcohol)/PVA and the difficulties related to the emulsion polymerization of hydrophobic monomers and the use of PVA having a high degree of hydrolysis (> 92%), the synthesis of new PVA based polymeric stabilizers for use in emulsion and miniemulsion polymerizations becomes very attractive and challenging. The aim of this work was to synthesize a new class of polymeric stabilizer, poly(vinyl alcohol-co-vinyl neo-decanoate)/PVA-VV, with a high degree of hydrolysis and differentiated properties to be used as stabilizers in the emulsion and miniemulsion copolymerization of vinyl acetate (VAc) with vinyl neo-nonanoate (VEOVA-9), that can be used as adhesive for wood bonding. New PVA based polymeric stabilizers with high degree of hydrolysis (94 - 98%) were synthesized in two steps: i) solution copolymerization of vinyl acetate (VAc) with vinyl neo-decanoate (VEOVA-10) and ii) alkaline hydrolysis (NaOH/Methanol) of poly(vinyl acetate-co-vinyl neodecanoate). Miniemulsions of VAc/VEOVA-9 were prepared using the different polymeric stabilizers in a "Manton Gaulin" high pressure homogenizer. The effect of different initiators (ammonium persulfate/APS or tert-butyl hydro peroxide/TBHP and tert-butyl peroxide benzoate/TBPB in the presence of sodium formaldehyde sulfoxylate/SFS) in the polymerization kinetic was evaluated. The effect of the type and concentration of polymeric stabilizer, in the emulsification step (average diameter of drops, stability of miniemulsions) as well in the polymerizations (rate of consumption of monomers, particle size and particles number) was investigated in this work. The partition of the polymeric stabilizers between the aqueous phase and the polymer particle surface (grafted/adsorbed) was determined and correlated with the viscosity and colloidal stability of latexes. Latexes with differentiated properties such as low-viscosity, lower grits content and improved storage stability, were obtained by miniemulsion polymerization with an ideal condition copy (1:1) of the monomer droplets to the polymer particles.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMT10002.pdf (8.31 Mbytes)
Fecha de Publicación
2012-10-04
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.