Disertación de Maestría
DOI
10.11606/D.97.2018.tde-03122018-180838
Documento
Autor
Nombre completo
Aline Aparecida Antunes Cornetti
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2018
Director
Tribunal
Milagres, Adriane Maria Ferreira (Presidente)
Prata, Arnaldo Márcio Ramalho
Ebinuma, Valéria de Carvalho Santos
Masarin, Fernando
Título en portugués
Caracterização das xilanas extraídas do bagaço de cana-de-açúcar pré-tratado como insumos potenciais para indústria de papel e celulose
Palabras clave en portugués
Adsorção
Bagaço de cana-de-açúcar
Sulfito alcalino
Xilana
Xilanase
Resumen en portugués
Em uma fábrica de celulose, a maioria da hemicelulose é dissolvida no licor negro e se queima no processo de recuperação de álcalis. Devido a isto, a reposição das hemiceluloses dissolvidas de volta à fibra é uma das alternativas para a retenção de hemicelulose nas polpas, o que aumenta o rendimento do processo e produz polpas de alta qualidade. O Brasil é o maior produção de cana-de-açúcar do mundo, o bagaço gerado em grande quantidade constitui uma potencial fonte barata e abundante de hemicelulose para uso em processos biotecnológicos. O aproveitamento desta fração do material lignocelulósico pode aumentar o valor comercial do bagaço de cana-de-açúcar. Nesse estudo, extraiu-se enzimaticamente a hemicelulose do bagaço visando utilizá-la como aditivos na indústria de papel e celulose. Inicialmente, o bagaço foi pré-tratado pelo processo quimiotermomecânico, em solução sulfito alcalino (10% Na2SO3 e 5% NaOH), 120 oC, 2 h. O pré-tratamento removeu 49,1% de lignina e 16,1% de xilana do bagaço, houve uma pequena solubilização de glucana (9,0%) e alto rendimento de sólidos (73,6%). A extração enzimática das xilanas a partir do bagaço pré-tratado foi feita com 5 UI de xilanase comercial (Luminase) por grama de material, em tampão fosfato 50 mM, 50 ºC, pH 8 por 6 e 24 horas, obtendo-se 15% e 28% de rendimento de xilana, respectivamente, determinada quimicamente pelos conteúdos de xilose e arabinose. As xilanas solubilizadas do bagaço pré-tratado com a xilanase comercial por 6 horas foram precipitadas em 15% e 30% de etanol. Recuperou-se 2 frações, denominadas Xilanas 1 e 2, que apresentaram massas molares médias de 34.180 g/mol e 28.130 g/mol, respectivamente, e grau de substituição mais elevado (0,16-0,19). O restante do material foi concentrado e denominado Xilana 3. As xilanas extraídas enzimaticamente por 24 horas foram liofilizadas e denominada Xilana 4. As Xilanas 3 e 4 possuem características semelhantes, como baixas massas molares (2.890-3.660 g/mol) e graus de substituição (0,13-0,14), porém com grandes quantidades de impurezas. As xilanas obtidas foram submetidas ao processo de adsorção em polpas celulósicas "kraft" de eucalipto, marrom e deslignificada, em pH 10, consistência de 5% (m/v) e 10% de relação xilana/celulose (m/m). A adsorção em celulose ocorreu para as xilanas com menor grau de substituição e o aumento da concentração de xilanas com menores massas molares aumentou as taxas de adsorção. Em função desses resultados, conclui-se que a extração enzimática de bagaço de cana-de-açúcar pré-tratado quimiotermomecanicamente com sulfito alcalino produziu majoritariamente xilanas de baixa massa molar e pouco substituídas, que foram eficientes durante processo de adsorção à polpa celulósica e podem ser exploradas para redeposição em polpa celulósica visando melhorar as características da fibra e aumentar o rendimento do processo.
Título en inglés
Characterization of xylans extracted from pre-treated sugarcane bagasse as inputs for the pulp and paper industry
Palabras clave en inglés
Adsorption
Alkaline sulfite
Sugarcane bagasse
Xylan
Xylanase
Resumen en inglés
In a celulose pulp factory, most of the hemicellulose are dissolved in the black liquor and burn in the alkali recovery process. For this reason, the replacement of the dissolved hemicelluloses back to the fiber is one of the alternatives for the retention of hemicellulose in the pulps, which increases the yield of the process and produces high quality pulps. Brazil has the largest sugarcane crop in the world, the bagasse generated in large quantities constitutes a potential cheap and abundant source of hemicellulose for use in biotechnological processes. The utilization of this fraction of the lignocellulosic material can increase the commercial value of sugarcane bagasse. In this study, hemicellulose was extracted enzymatically from the bagasse to be used as additives in the pulp and paper industry. Initially, the bagasse was pretreated by the chemothermomechanical process, in alkaline sulfite solution (10% Na2SO3 and 5% NaOH), 120 ?, 2h. The pretreatment removed 49.1% of lignin and 16.1% of xylan from the bagasse, there was a small solubilization of glucan (9.0%) and high solids yield (73.6%). Enzymatic extraction of xylan from pretreated bagasse was made with 5 IU of commercial xylanase (Luminase) per gram of material, in 50 mM phosphate buffer, 50 °C, pH 8 by 6 and 24 hours, obtaining 15% and 28% xylan yield, respectively, determined chemically by the contents of xylose and arabinose. The solubilized xylans of pre-treated bagasse with the commercial xylanase for 6 hours were precipitated in 15% and 30% ethanol. Two fractions, named Xylans 1 and 2, were recovered, having average molar masses of 34.180 g/mol and 28.130 g/mol, respectively, and a higher degree of substitution (0,16-0,19). The remainder material was concentrated and named Xylan 3. Xylans extracted enzymatically for 24 hours were lyophilized and named Xylan 4. Xylans 3 and 4 had the same similar characteristics as low molar masses (2.890-3.660 g / mol) and degrees of substitution (0,12-0,14), but with large amounts of impurities. The xylans were submitted to the adsorption process in cellulosic pulps of eucalyptus, brown and delignified, in pH 10, consistency of 5% (m/v) and 10% ratio xylan mass/cellulose mass (m/m). The adsorption in cellulose occurred for the xylan with lower degree of substitution and the increase of the xylan concentration with smaller molar masses increased the adsorption rates. Based on the results, it was concluded that the enzymatic extraction of sugarcane bagasse pretreated chemothermically with alkali sulphite produced mainly xylans of low molar mass and degree of substitution, which were efficient during the adsorption process to the cellulosic pulp and can be used for redeposition in cellulosic pulp in order to improve the characteristics of the fiber and increase the process yield.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
BID18003_C.pdf (4.22 Mbytes)
Fecha de Publicación
2018-12-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.