Mémoire de Maîtrise
DOI
10.11606/D.88.2009.tde-31032009-103653
Document
Auteur
Nom complet
Daniel Komatsu
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2009
Directeur
Jury
Canale, Lauralice de Campos Franceschini (Président)
Agustinho, Sylvana Cardoso Miguel
Farah, Alessandro Fraga
Titre en portugais
Estudo do comportamento do óleo de soja como fluido de têmpera na presença de aditivos anticorrosivos
Mots-clés en portugais
Anticorrosivo
Corrosão
Óleo de soja
Tratamento térmico de têmpera
Resumé en portugais
Estuda o desempenho de diferentes anticorrosivos, adicionados ao óleo de soja aditivado com o Irganox L 109, um antioxidante. O objetivo é verificar qual deles oferece melhor proteção ao latão e ao aço, simultaneamente. Ensaios de perda de massa e análise potenciodinâmica foram feitos com essa finalidade. Essas formulações foram caracterizadas com ensaios de viscosidade, curvas de resfriamento, espectroscopia de infravermelho e ângulo de contato. O estudo se estendeu, também, para o óleo de soja puro (sem adição de aditivos). Essas formulações de óleo de soja com diferentes concentrações de anticorrosivos e com uma concentração fixa de antioxidante foram submetidas a um processo de envelhecimento acelerado e após isso, foram novamente realizados os ensaios citados anteriormente. Com isso, pode-se comparar qual das formulações sofreu a menor variação na sua propriedade. Com isso, pode-se verificar que a formulação 0,1% 2-mercaptobenzotiazol foi a que apresentou o melhor comportamento para a finalidade requerida.
Titre en anglais
Study behavior of soybean oil as a quenching fluid in the presence of anticorrosion additives
Mots-clés en anglais
Anticorrosion
Corrosion
Heat Treatment
Soybean oil
Resumé en anglais
This work presents studies the performance of different anticorrosion additives, that were added in a composition of soybean oil and antioxidant Irganox L 109. The objective was determine which one offers good protection to the brass and steel, simultaneously. Tests of loss mass and potentiodynamic analysis were performed for this purpose. These formulations were characterized with tests of viscosity, cooling curves, infrared spectroscopy and contact angle measures. Similar studies were also extended to the pure soybean oil (without additives). The soybean oil formulations (different anticorrosion concentrations and fixed antioxidant concentration) were subjected to process of accelerated aging (oxidation) and new characterization tests were performed again. Comparative analyses between before and after oxidation tests were performed in order to verify which formulation had less variation on the properties. Results shown formulation 0.1% 2-Mercaptobenzothiazole has the best behavior for the purpose required.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
daniel.pdf (2.09 Mbytes)
Date de Publication
2009-04-08
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.