Disertación de Maestría
DOI
10.11606/D.88.2009.tde-31032009-103653
Documento
Autor
Nombre completo
Daniel Komatsu
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2009
Director
Tribunal
Canale, Lauralice de Campos Franceschini (Presidente)
Agustinho, Sylvana Cardoso Miguel
Farah, Alessandro Fraga
Título en portugués
Estudo do comportamento do óleo de soja como fluido de têmpera na presença de aditivos anticorrosivos
Palabras clave en portugués
Anticorrosivo
Corrosão
Óleo de soja
Tratamento térmico de têmpera
Resumen en portugués
Estuda o desempenho de diferentes anticorrosivos, adicionados ao óleo de soja aditivado com o Irganox L 109, um antioxidante. O objetivo é verificar qual deles oferece melhor proteção ao latão e ao aço, simultaneamente. Ensaios de perda de massa e análise potenciodinâmica foram feitos com essa finalidade. Essas formulações foram caracterizadas com ensaios de viscosidade, curvas de resfriamento, espectroscopia de infravermelho e ângulo de contato. O estudo se estendeu, também, para o óleo de soja puro (sem adição de aditivos). Essas formulações de óleo de soja com diferentes concentrações de anticorrosivos e com uma concentração fixa de antioxidante foram submetidas a um processo de envelhecimento acelerado e após isso, foram novamente realizados os ensaios citados anteriormente. Com isso, pode-se comparar qual das formulações sofreu a menor variação na sua propriedade. Com isso, pode-se verificar que a formulação 0,1% 2-mercaptobenzotiazol foi a que apresentou o melhor comportamento para a finalidade requerida.
Título en inglés
Study behavior of soybean oil as a quenching fluid in the presence of anticorrosion additives
Palabras clave en inglés
Anticorrosion
Corrosion
Heat Treatment
Soybean oil
Resumen en inglés
This work presents studies the performance of different anticorrosion additives, that were added in a composition of soybean oil and antioxidant Irganox L 109. The objective was determine which one offers good protection to the brass and steel, simultaneously. Tests of loss mass and potentiodynamic analysis were performed for this purpose. These formulations were characterized with tests of viscosity, cooling curves, infrared spectroscopy and contact angle measures. Similar studies were also extended to the pure soybean oil (without additives). The soybean oil formulations (different anticorrosion concentrations and fixed antioxidant concentration) were subjected to process of accelerated aging (oxidation) and new characterization tests were performed again. Comparative analyses between before and after oxidation tests were performed in order to verify which formulation had less variation on the properties. Results shown formulation 0.1% 2-Mercaptobenzothiazole has the best behavior for the purpose required.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
daniel.pdf (2.09 Mbytes)
Fecha de Publicación
2009-04-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.