Tese de Doutorado
DOI
10.11606/T.88.1996.tde-29012010-160947
Documento
Autor
Nome completo
Samuel Jose Casarin
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1996
Orientador
Banca examinadora
Rollo, Joao Manuel Domingos de Almeida (Presidente)
Goldenstein, Helio
Gregolin, José Ângelo Rodrigues
Mei, Paulo Roberto
Spinelli, Dirceu
Título em português
Caracterização da temperabilidade de um aço C-Mn microligado ao boro, através de dilatometria e curvas de transformações de fases por resfriamento contínuo.
Palavras-chave em português
Aços ao boro
Curvas CCT
Dilatometria
Transformações de fases
Resumo em português
No presente trabalho, foi realizado um estudo sobre a influência da adição do boro em um aço C-Mn, nas transformações de fases por resfriamento contínuo, através da técnica dilatométrica. Para este estudo, utilizou-se dois aços de composição química semelhante: o aço 10B22 com 30 ppm de boro e o aço sem boro é o E1522, equivalente. Foram traçadas as curvas de CCT dos dois aços, onde analisou-se o efeito de temperabilidade do boro através das curvas de resfriamento. Os materiais foram ensaiados em um dilatômetro de resfriamento rápido, utilizando corpos de prova cilíndricos, resfriados por injeção de ar e hélio. Os resultados gráficos dos processos de resfriamento foram comparados com análises metalográficas ótica estruturais e quantitativas e também por medidas de dureza. Detalhes microestruturais, tais como, contagem de fases formadas em função das taxas de resfriamento, tamanho de grão, distribuição de inclusões e precipitados, foram extraídos, através de um sistema de análise de imagens. Complementando o trabalho, foi realizado uma completa documentação fotográfica das microestruturas, com uma indicação final do tratamento térmico mais adequado aos aços C-Mn microligados ao boro.
Título em inglês
C-Mn boron microalloyed steel hardenability characterization throught dilatometry and continuous cooling transformations curves.
Palavras-chave em inglês
Boron steels
CCT curves
Dilatometry
Phase transformation
Resumo em inglês
This work presents a study about the influence of boron on phase transformation by continuous cooling in a C-Mn steel using the dilatometric technique. For this study two close chemical composition steels were applied: a 10B2 steel with 30 ppm of boron and a E1522 steel without boron. For both steels the CCT curves were obtained, where the effect of boron on hardenability was analysed throughout continuous cooling curves. Both materials were testedcin a high speed quenching dilatometer, using cilindricals samples quenched by helium blow on their surfaces. The graphics results of cooling processes were compared with microstructural and quantitative optical metallographic analysis and hardness measurements. Microstructural features as such phases fraction as a function of cooling rates, grain size, and distributions of inclusions and precipitates were obtained through an image analysis system. In addition, complete microstructural photography documentation was carried out where it was possible to indicate the best heat treatment to boron microalloyed C-Mn steels.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
SamuelJoseCasarinD.pdf (16.89 Mbytes)
Data de Publicação
2010-02-23
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.