• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Thèse de Doctorat
DOI
10.11606/T.88.2001.tde-25042002-092742
Document
Auteur
Nom complet
Inacio Regiani
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2001
Directeur
Jury
Souza, Milton Ferreira de (Président)
Bressiani, José Carlos
Hernandes, Antonio Carlos
Rodrigues, José de Anchieta
Tomasi, Roberto
Titre en portugais
"Películas Espessas de Carbeto de Silício, SiC, sobre Mulita"
Mots-clés en portugais
Deposição química por Vapor (CVD)
mulita
SiC
terras raras
whiskers
Resumé en portugais
Filmes de carbeto de silício, SiC, cristalinos foram depositados sobre peças de mulita por meio da técnica de deposição química por vapor (CVD) a pressão atmosférica. As características da superfície do substrato determinam se o filme será denso ou poroso, enquanto a temperatura define a cristalinidade e a taxa de nucleação para formação do filme. Durante os procedimentos de preparação do substrato de mulita para a deposição do filme, observou-se o fenômeno da formação de whiskers de mulita quando adicionados 3%mol de terras raras a peça. O fenômeno de crescimento destes whiskers foi sistematicamente estudado para sua caracterização e compreensão do mecanismo de formação. A adição de terras raras promoveu um abaixamento na temperatura de mulitização e a formação de whiskers com uma composição cuja razão alumina / sílica é de 1,3, uma das mais baixas observadas.
Titre en anglais
Silicon carbide, SiC, thick films over mullite.
Mots-clés en anglais
Chemical Vapor Deposition (CVD)
mullite
rare earth
SiC
whiskers
Resumé en anglais
Crystalline silicon carbide, SiC, films were deposited on mullite by atmospheric pressure chemical vapor deposition (CVD) method. The characteristic of substrate surface determinate if the film will be dense or porous, while the deposition temperature defines its crystalinity and nucleation rate in film formation. During the mullite substrate preparation process for film deposition, it was observed a whisker formation phenomenon when the piece was doped with 3%mol of rare earth. The growth phenomenon of these whiskers was studied systematically to its characterization and comprehension of its formation mechanism. The addiction of rare earth promote a reduction in mullitization temperature and the formation of whiskers with a composition that alumina / silica ration was 1.3, one of the lowest one ever observed.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
parte1-teseinacio.pdf (94.66 Kbytes)
parte2-teseinacio.pdf (1.95 Mbytes)
parte3-teseinacio.pdf (1.20 Mbytes)
parte4-teseinacio.pdf (3.50 Mbytes)
parte5-teseinacio.pdf (2.37 Mbytes)
parte6-teseinacio.pdf (253.26 Kbytes)
signifie que le fichier ne peut être consulté à l'intérieur du Unversité de São Paulo.
Date de Publication
2004-04-30
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.