Disertación de Maestría
DOI
10.11606/D.88.2002.tde-17032004-163144
Documento
Autor
Nombre completo
Omar Maluf
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2002
Director
Tribunal
Spinelli, Dirceu (Presidente)
Ruffino, Rosalvo Tiago
Sordi, Vitor Luiz
Título en portugués
"Influência do roleteamento no comportamento em fadiga de um ferro fundido nodular perlítico"
Palabras clave en portugués
fadiga
ferro fundido nodular
roleteamento
tensão residual
Resumen en portugués
O processo de roleteamento é um tratamento superficial, comumente utilizado em peças fabricadas em aços e ferros fundidos nodulares, em regiões onde há concentradores de tensões, com o intuito de melhorar as propriedades de resistência à fadiga. Este processo endurece e introduz tensões residuais compressivas na camada superficial do material, através de deformação controlada, provocando uma redução das tensões de tração que atuam na superfície da peça submetida a carregamentos cíclicos. Este trabalho teve como principal objetivo o estudo do efeito do roleteamento superficial sobre o comportamento em fadiga de um ferro fundido nodular de matriz perlítica, utilizado na fabricação de virabrequins pela indústria automobilística. Foram realizados ensaios de fadiga por flexão rotativa em corpos de prova lisos e com entalhe. Os corpos de prova com entalhe foram divididos em dois grupos, com e sem roleteamento superficial. Foi utilizado entalhe com geometria semicircular com raio de 1,20mm e profundidade de 0,70mm. Para o processo de roleteamento foi utilizado um rolete com diâmetro de 15,00mm e com raio de curvatura de 1,30mm e aplicada uma força de compressão de 2390N. A introdução de tensões residuais compressivas pelo trabalho a frio, dificultou a nucleação e a propagação de trincas na camada superficial dos entalhes roleteados. Isto ficou evidenciado pelo aumento do valor do limite de fadiga para 483MPa obtido para o material entalhado e roleteado, enquanto que para o material nas condições de sem entalhe e somente entalhado estes valores foram de 300MPa e 168Mpa, respectivamente.
Título en inglés
The effect of surface rolling on fatigue behavior in a pearlitic ductile cast iron
Palabras clave en inglés
ductile cast iron
fatigue
residual stress
surface rolling
Resumen en inglés
Surface rolling is a mechanical treatment commonly used in parts fabricated with steel and ductile cast iron, specifically in stress concentration regions, to improve fatigue properties. This process hardens and introduces compressive residual stresses to the surface of the material through the application of controlled strains, thus provoking a reduction of resulting tensile stress at its surface under cyclic loading. This work deals with the effect of surface rolling on high cycle fatigue behavior of a pearlitic ductile cast iron used in crankshaft by automotive industries. Rotating bending fatigue tests were performed in both smooth and notched specimens. The notched specimens were divided into two groups: with and without surface rolling treatment. The specimens notch geometry was semicircular with radius of 1.20mm and depth of 0.70mm. The rolling treatment was carried out using a roller with diameter of 15,00mm, curvature radius of 1.30mm and a compression force of 2390N. The introduction of compressive residual stresses under cold work made difficult the nucleation and propagation of the crack on the rolled surface of the notch. It was confirmed by the increase of the endurance limit of the surface rolled specimens to 483MPa in comparison with the smooth and notched specimens, respectively, 300MPa and 168 MPa.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
dissomar.pdf (4.14 Mbytes)
Fecha de Publicación
2004-08-02
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.