Disertación de Maestría
DOI
10.11606/D.88.2006.tde-14112014-085552
Documento
Autor
Nombre completo
Ritamara Isis de Mattos
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2006
Director
Tribunal
Gonzalez, Jose Pedro Donoso (Presidente)
Maule, Agnieszka Joanna Pawlicka
Ribeiro, Sidney José Lima
Título en portugués
Estudo da influência da umidade nas propriedades de transporte dos eletrólitos poliméricos obtidos de amido plastificado
Palabras clave en portugués
Amido plastificado
Eletrólitos poliméricos
Ressonância magnética nuclear
Resumen en portugués
Neste trabalho foi estudado o eletrólito sólido polimérico obtido através da plastificação do amido rico em amilopectina com glicerol em porcentagem de 30% em ralação a massa do amido utilizado, e contendo perclorato de litio (LiClO4), com uma razão [0]/[Li] = 10 (AGL). Com o objetivo de estudar a influência da umidade relativa nas propriedades de transporte iônico do eletrólito, foi utilizada a técnica de Ressonância Magnética Nuclear RMN. Neste trabalho, também, foram utilizadas outras técnicas de caracterização como: DSC, TGA e condutividade A.C. No estudo de RMN, foram realizadas medidas da forma de linha e da taxa de relaxação spin-rede do 1H e do 7Li em função da temperatura, a fim, de estudar a mobilidade do próton e do íon lítio no complexo polimérico. Os resultados desacoplamento do 7Li {1H} medidos na temperatura de 183K mostraram que 80% da largura de linha foi atribuída a interação heteronuclear Li-H. Os resultados da relaxação mostraram um aumento na mobilidade do complexo polimérico e do íon lítio com o aumento da hidratação do eletrólito. Os valores para a energia de ativação são da ordem de 0.20eV para o próton e 0.23eV para o lítio, consistente com os valores encontrados em outros eletrólitos sólidos poliméricos (0.2 - 0.3eV)
Título en inglés
Study of the humidity influence on the transport properties of plastified amide based polymer electrolytes
Palabras clave en inglés
NMR
Plastified amide
Polymer electrolytes
Resumen en inglés
In this work we report the study of solid polymer electrolyte obtained from amylopectin rich starch plasticized with 30% in mass of glycerol and lithium perchlorate (LiClO4) with a reason [0]/[Li] = 10. With the objective to study the influence of the relative humidity in the properties of ionic transport of the electrolyte, the technique of Nuclear Magnetic Resonance - NMR was used. The samples were also characterized by DSC, TGA and A.C. conductivity. The mobility of protons and lithium ion were study through the temperature dependence of 1H and 7Li NMR lineshape and spin-lattice relaxation times. The 7Li {1H} decoupling results measured in the temperature of 183K, shows that 80% of the width of line was attributed to Li-H heteronuclear interaction. The relaxation results showed an increase of mobility of proton and lithium ion in the polymer complex with the increase of the relative humidity of the electrolyte. Activation energy of the arder of 0.20eV for the proton and 0.23eV for lithium were obtained from NMR measurements, consistent with the values found in other solid polymer electrolyte (0,2 - 0.3eV)
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-11-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.