• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
https://doi.org/10.11606/D.88.2016.tde-14092016-164708
Documento
Autor
Nombre completo
Cleyton Fernandes Ferrarini
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1998
Director
Tribunal
Canale, Lauralice de Campos Franceschini (Presidente)
Gomes, Samuel Irati Novaes
Zavaglia, Cecília Amélia de Carvalho
Título en portugués
Análise da resistência ao desgaste abrasivo de um revestimento duro obtido pela deposição, por soldagem, de uma liga a base de ferro
Palabras clave en portugués
Abrasão
Desgaste
Liga ferrosa
Revestimento duro
Resumen en portugués
O presente trabalho apresenta a análise da resistência ao desgaste abrasivo de um revestimento duro e do aço SAE 5160. O revestimento foi obtido pela deposição de uma liga ferrosa através de processo de soldagem "TIG" sobre um aço ABNT 1020. Aliga foi desenvolvida com a utilização de CR e Nb como elementos formadores de carbonetos, proporcionando uma microestrutura constituída, no estado bruto de fusão, de uma rede de carbonetos (Cr, Fe)7C3 interdendríticos e NbC dispersos em uma matriz austenítica. Corpos de prova revestidos foram submetidos a tratamentos térmicos de normalização, têmpera, sub-zero e revenido, visando a obtenção de diferentes microestruturas na matriz, enquanto que o aço SAE 5160 foi temperado e revenido de acordo com o procedimento utilizado na confecção de ferramentas agrícolas com este material. A resistência ao desgaste do revestimento foi superior à do aço SAE 5160 nos dois tipos de ensaios de abrasão realizados, sendo os melhores desempenhos apresentados pelo revestimento temperado no ensaio realizado com equipamento do tipo pino sobre lixa e pelo revestimento temperado e revenido no ensaio do tipo roda de borracha/areia seca. A identificação dos mecanismos de remoção de material predominantes nos ensaios abrasivos foi possibilitada pela observação das superfícies desgastadas dos corpos de prova através de microscopia eletrônica de varredura.
Título en inglés
Analysis of the abrasive wear resistance of a hardfacing obtained through the deposition by the welding of an iron based alloy
Palabras clave en inglés
Abrasion
Hardfacing
Iron based alloy
Wear
Resumen en inglés
The present work presents an analysis of the abrasive wear resistance of a hardfacing and of the SAE 5160 steel. The hardfacing was obtained by the deposition of a iron based alloy through "TIG" welding on a ABNT 1020 steel. This alloy was developed with the use of Cr and Nb as carbide forming elements , resulting in a microstructure formed by a carbide net of M7C3 interdendritic in a austenitic matrix. The hardfacing samples suffered heat treatment of normalizing, hardening, tempering and subzero, viewing the achievement of differents microstructure, while the SAE 5160 steel suffered hardening and tempering according to the production process used in the agricutural tool manufacturing. The wear resistance of the hardfacing overcame the SAE 5160 steel in both types of abrasion wear tests, and the best performances were presented by hardening hardfacing in the pin wear test and by the tempering hardfacing in the rubber wheel/dry sand test. The identification of the material removal mechanisms in the abrasive tests was made by the observation of the worn surfaces of the samples through the scanning eletronic microscopy.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-09-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.