Tesis Doctoral
DOI
10.11606/T.88.2000.tde-13062012-151141
Documento
Autor
Nombre completo
Aluísio Bráz de Mélo
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2000
Director
Tribunal
Liborio, Jefferson Benedicto Libardi (Presidente)
Barros, Mercia Maria Semensato Bottura de
Helene, Paulo Roberto do Lago
Sichieri, Eduvaldo Paulo
Souza, Milton Ferreira de
Título en portugués
Influência da cura térmica (vapor) sob pressão atmosférica no desenvolvimento da microestrutura dos concretos de cimento Portland
Palabras clave en portugués
Adições
Concreto de alto desempenho
Concreto de cimento Portland
Cura térmica
Etringita secundária
Microestrutura
Resistência mecânica
Resumen en portugués
Os investimentos iniciais em moldes na indústria de pré-moldados de concreto de cimento Portland, em geral, são altos, havendo a necessidade de utilizá-los o mais intensivamente possível entre uma e outra moldagem. A conseqüência é que a desforma pode ocorrer em instantes inadequados, comprometendo a durabilidade do produto. Isto contraria o conceito fundamental da pré-moldagem que está relacionado ao rigoroso controle de qualidade do produto. A cura térmica é uma alternativa, pois é utilizada para acelerar a resistência mecânica inicial do concreto. Esse beneficio imediato é acompanhado por uma redução na resistência final comparativamente à cura normal em câmara úmida. Esta redução é atribuída ao desenvolvimento de uma microestrutura modificada. Para investigar esse fenômeno, com base nos conhecimentos em ciência e engenharia dos materiais, desenvolve-se um estudo experimental, aplicado a pré-moldados com pequena espessura. O objetivo principal é analisar tais modificações e os compostos hidratados, formados ao longo do tempo após a cura térmica, considerando os materiais empregados e estabelecendo relações com a perda de resistência final. Leva-se em conta a influência das adições e da duração dos ciclos térmicos. A análise da microestrutura está baseada nos seguintes ensaios: porosimetria por intrusão de mercúrio, microscopia eletrônica de varredura, termogravimetria e difração de raio-X. Confirma-se com base nos resultados que a cura térmica favorece a maior formação de portlandita e também acelera a reação pozolânica. Para a composição entre cimento Portland, a escória de alto forno (30%) e a sílica ativa (10%), submetidas a ciclos térmicos longos (12 horas Tmax=61°C), observa-se a maior perda na resistência mecânica a longo prazo. Neste caso, há fortes indícios de que há formação de fases com menor desempenho mecânico. Através de micrografias, para essa amostra, sugere-se a formação da etringita secundária com maior prejuízo na interface pasta-agregado. As conclusões sugerem que para minimizar as interferências no processo de cura e garantir resistências mínimas nas desmoldagens rápidas, com poucas perdas a longo prazo, é interessante associar ciclos térmicos curtos, cimento de alta resistência inicial, sílica ativa e superplastificante.
Título en inglés
The influence of steam curing in development of microstructure of Portland cement concrete
Palabras clave en inglés
Additions
High performance concrete
Microstructure
Portland cement concrete
Secondary ettringite
Steam curing
Strenght
Resumen en inglés
The initial investments of molds in the industry which makes pre-cast of Portland cement concrete is usually very high, thus creating a necessity to maximize the utilization of each moldings. The consequence is that the forms can be removed at inadequate time, which compromise the durability of the product. This contradicts the fundamental concepts of the pre-castings, which is related to a severe quality control. Steam curing is an alternative treatment and is used to accelerate the initial mechanical resistance of the concrete. This immediate benefit is accompanied by the decrease on final resistance compared to normal curing in humid chamber. This reduction is attributed to the development of a modified microstructure. To investigate this phenomenon, based on knowleledge of materials science and engineering, an experimental study is developed which is applied in pre-cast wich small thichness. The main objective of this work is to analyze the microstructure modifications and the hydrated compounds formed, after a period of steam curing, taking in account the used materiaIs, also to establish a relations with the loss of final strength. The influence of additions and duration of steam cycles are considered. The analyses of microstructures are based on the following tests: mercury intrusion porosimetry, scanning electron microscope, thermogravimetry and X-ray diffraction. Based on the results it can be confirmed that steam curing favors a large formation of ponlandite and also accelerates pozzolanic reaction. For the composition of Portland cement, slag fumace blast (30%) and active silica (10%), submitted for long period of thermal cycles (12 hours, Tmax=61°C), a great loss strength was observed. In this case it is possible the formation of phases with poor mechanical performance. Through micrographs, for this sample, it is observed the formation of secondary ettringite with a large damage in the interface aggregate-paste. The conclusions suggest that to minimize the interference in the process of curing and to guarantee a minimum strength during the rapid separation of the concrete from the molds, with a minor loss in a long term, it is interesting to associate short steam cycles, high initial resistance cement, adive silica and superplasticizer.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
AluisioBrazdeMeloD.pdf (38.87 Mbytes)
Fecha de Publicación
2012-08-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.