Disertación de Maestría
DOI
10.11606/D.88.2009.tde-13052009-111648
Documento
Autor
Nombre completo
Luís Fernando da Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2009
Director
Tribunal
Mastelaro, Valmor Roberto (Presidente)
Goncalves, Debora
Scalvi, Luis Vicente de Andrade
Título en portugués
Síntese e Caracterização do Composto SrTi1-xFexO3 Nanoestruturado
Palabras clave en portugués
1. Perovskitas. 2. SrTi1xFexO3 nanoestruturado. 3. Pechini. 4. Caracterização estrutural. 5. Morfolo
Resumen en portugués
Este trabalho reporta a síntese de amostras cerâmicas e filmes finos nanoestruturados de composição SrTi1-xFexO3 (0,0 < x < 0,75) através do método dos precursores poliméricos modificado. A influência da adição de ferro nas propriedades térmicas, estruturais e morfológicas do composto SrTiO3 foi investigada através das técnicas de termogravimetria, análise térmica diferencial, difração de raios X, espectroscopia de absorção de raios X, de infravermelho e Raman, e microscopia eletrônica de varredura e transmissão. As medidas de análise térmica mostraram que a adição de ferro a rede do SrTiO3 levou a uma redução na temperatura de decomposição e de cristalização do material precursor. Medidas de difração de raios X indicaram a diminuição do parâmetro de rede e do tamanho dos cristalitos com o aumento da quantidade de ferro. A análise dos espectros de absorção de raios X mostrou a predominância de íons Fe3+. Em relação à microestrutura das amostras na forma de pó, foi observado que o aumento da quantidade de ferro levou a uma sinterização parcial das nanopartículas e ao crescimento dos grãos. Modificações na atmosfera e na temperatura de calcinação do composto SrTiO3 não dopado evitaram a formação de pescoços entre as nanopartículas que apresentaram uma maior uniformidade com tamanhos da ordem de 11 nm. Filmes finos de composição SrTiO3 e SrTi1-xFexO3 depositados pela técnica de dip-coating apresentaram uma única fase cristalina e uma boa adesão ao substrato. Medidas de microscopia de força atômica (AFM) indicaram uma redução da rugosidade superficial dos filmes com o aumento da quantidade de ferro.
Título en inglés
Synthesis and Characterization of Nanostructured SrTi1-xFexO3
Palabras clave en inglés
1.Perovskite. 2. Nanostructured SrTi1-xFexO3. 3. Pechini. 4. Structural characterization. 5. Morphol
Resumen en inglés
This work reports the synthesis of nanostructured SrTi1-xFexO3 powder and thin films (0.0 < x < 0.75) using a modified polymeric precursor method. The influence of the addition of iron in thermal, structural and morphological properties of SrTiO3 compound was investigated by thermogravimetry (TG), differential thermal analysis (DTA), X-ray diffraction (XRD), X-ray absorption, Raman and infrared spectroscopies and scanning and transmission electron microscopy techniques. DTA and TG results showed that the addition of iron into the SrTiO3 network leads to a reduction of the decomposition and crystallization temperatures of the precursor powder. The analysis of the X-ray diffraction patterns indicated the reduction of the crystallite sizes and the lattice parameters with the increase of the iron amount. The analysis of the absorption spectra at the Fe K-edge of the nanoparticle samples indicates the predominance of Fe3+ ions. The increase of the amount of iron also leads to a partial sintering of the nanoparticles. Changes in the atmosphere and in the temperature of calcination of undoped SrTiO3 prevented the formation of necks between the nanoparticles and showed a greater uniformity in the particle size around 11 nm. Thin films of SrTiO3 and SrTi1-xFexO3 deposited by dip-coating onto amorphous substrate showed the formation of a single crystalline phase and good adhesion to the substrate. AFM measurements indicated a reduction in the surface roughness as the amount iron increases.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
dissertacao.pdf (3.46 Mbytes)
Fecha de Publicación
2009-05-20
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • Silva, L. F., et al. Synthesis and thermal decomposition of SrTi1?x Fe x O3 (0.0 ? x ? 0.1) powders obtained by the polymeric precursor method [doi:10.1007/s10973-009-0241-y]. Journal of Thermal Analysis and Calorimetry [online], 2009, vol. 97, p. 173-177.
  • Silva, L. F., et al. Synthesis and thermal decomposition of SrTi1?x Fe x O3 (0.0 ? x ? 0.1) powders obtained by the polymeric precursor method [doi:10.1007/s10973-009-0241-y]. In 14th ICTAC - International Congress on Thermal Analysis and Calorimetry, Poços de Caldas. Proceedings of the 14th ICTAC - International Congress on Thermal Analysis and Calorimetry., 2009.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.