Tesis Doctoral
DOI
10.11606/T.88.2004.tde-11092007-104457
Documento
Autor
Nombre completo
Gilmara de Oliveira Machado
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2004
Director
Tribunal
Pawlicka, Agnieszka Joanna (Presidente)
Gonzalez, Jose Pedro Donoso
Kawano, Yoshio
Oliveira Junior, Osvaldo Novais de
Torresi, Roberto Manuel
Título en portugués
Preparação e caracterização de eletrólitos sólidos poliméricos a partir dos derivados de celulose - hidroxietilcelulose e hidroxipropilcelulose
Palabras clave en portugués
Derivados de celulose
Eletrólitos sólidos poliméricos
Plastificação da HEC
Reação de entrecuzamento da HPC
Resumen en portugués
Esta tese apresenta os resultados da obtenção de eletrólitos sólidos poliméricos a partir dos derivados de celulose - hidroxipropilcelulose (HPC) e hidroxietilcelulose (HEC), ambas comerciais. Para atingir os objetivos do projeto, os dois derivados passaram por diferentes processos sendo que a HEC foi modificada fisicamente por meio de plastificação com glicerol e HPC foi alterada quimicamente. A transformação química consistiu nas reações de oxidação de grupos hidroxila da HPC em grupos cetona que, em seguida, foram submetidos as reações de enxertia com diamina de poli(óxido de propileno) [Jeffamina] resultando em redes por meio de ligações imina. A adição do sal perclorato de lítio, em diferentes concentrações, na matriz plastificada ou entrecruzada, resultou na obtenção de eletrólitos sólidos poliméricos, todos na forma de filmes. A caracterização destes eletrólitos foi realizada com técnicas básicas de caracterização de materiais como: análises térmicas (DSC, TGA), análise térmica dinâmico-mecânica (DMTA), análises estruturais (raios-X), medidas espectroscópicas (IR, UVNIS), análise elementar, microscopia eletrônica de varredura (SEM), e, como a mais importante, medidas de condutividade iônica utilizando a técnica de espectroscopia de impedância eletroquímica (EIS).
Título en inglés
Preparation and characterization of solid polymeric electrolytes based on hydroxypropylcellulose and hydroxyethlcellulose
Palabras clave en inglés
Cellulose derivatives
Networks of HPC
Plasticization process
Solid polymeric electrolyte
Resumen en inglés
The present thesis reports the preparation and characterization of new types of solid polymeric electrolytes (SPE) based on cellulose derivatives such as hydroxypropylcellulose (HPC) and hydroxyethylcellulose (HEC), both commercial products. Aiming to reach this purpose both derivatives were subjected to modification processes, where HEC were physically modified by plasticization process with glycerol and HPC were submitted to chemical reactions. The latter ones were promoted by the oxidation of HPC hydroxyl groups and ketone groups and then subjected to grafting with diamine poly(propylene oxide) (Jeffamine), resulting in the imine bond network formation. Different concentrations of lithium salt were added to the plasticized and grafted samples, resulting in solid polymeric electrolytes, all in the film form. The characterization of these samples was performed by thermal analysis (DSC, TGA and DMTA), X-ray diffraction (XDR), scanning electron microscopy (SEM), ultraviolet/visible/near-infrared spectroscopy (UV/Vis/NIR) and, as most important, measured of ionic conductivity using the technique of electrochemical impedance spectroscopy (EIS).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
GilmaraMachado.pdf (6.35 Mbytes)
Fecha de Publicación
2007-09-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.