Master's Dissertation
DOI
10.11606/D.88.2017.tde-11072017-152720
Document
Author
Full name
Valdirene Maria Silva
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2002
Supervisor
Committee
Liborio, Jefferson Benedicto Libardi (President)
Freire, Wesley Jorge
Spinelli, Dirceu
Title in Portuguese
Contribuição ao estudo da carbonatação em concretos e argamassas executados com e sem adição de sílica ativa
Keywords in Portuguese
Argamassa
Argamassa de alto desempenho
Carbonatação
Concreto
Concreto de alto desempenho
Construção civil
Deterioração
Patologia
Sílica ativa
Abstract in Portuguese
O presente estudo refere-se a uma das deteriorações mais freqüentes nas estruturas de concreto armado: a ação da carbonatação. Para essa verificação construiu-se uma câmara de carbonatação acelerada, que foi calibrada, com a finalidade de estudar o processo de carbonatação em corpos-de-prova executados em concreto e argamassa com cimentos CP V ARI Plus e CP V ARI RS com e sem adição de sílica ativa, curados em câmara úmida por sete dias e posteriormente expostos à atmosfera agressiva de gás carbônico por 7, 14, 28, 63 e 91 dias. Também foram executados corpos-de-prova semelhantes (controle), os quais foram ensaiados à compressão axial e à compressão diametral para determinação da resistência à compressão, tração e medida da profundidade de carbonatação. A partir destes resultados é ajustado um modelo teórico experimental para previsão da profundidade de carbonatação em função do tempo. Observa-se que para todas as composições estudadas a profundidade de carbonatação é pequena. Analisa-se também, a influência da carbonatação no ganho da resistência mecânica das argamassas e dos concretos, e o efeito da adição de sílica ativa e do tipo de cimento no fenômeno de carbonatação. Finalizando, é apresentada uma justificativa dos resultados com base no banco de dados existente no LMABC-SET-EESC-USP.
Title in English
Contribution to the carbonation study in concretes and mortars manufactured with and without the addition of silica fume
Keywords in English
Carbonation
Civil building
Concrete
Deterioration
High performance concrete
High performance mortar
Mortar
Pathology
Silica fume
Abstract in English
The present study refers to one of the most frequent deterioration in reinforced concrete structure: the action of carbonation. For this, an accelerated carbonation chamber was built and gauged in order to study the carbonation process in concrete and mortar specimens with CP V ARI Plus and CP V ARI RS cements, with and without silica fume addition. The specimens were cured in a humidity chamber for seven days and exposed to aggressive atmosphere of carbonic gas for 7, 14, 28, 63 and 91 days. Similar specimens of control were also manufactured and left in humidity chamber during the same periods. These specimens were tested an axial compression and splitting tensile strength to determine the compression and tensile strength and the carbonation depth. From all the obtained results an experimental theoretical model was forecasted to determine the depth carbonation in function of time. It is observed that all the depths carbonation measured is small. The carbonation influence on mechanical resistance gain of the mortar and concrete, as well as the effect addition of both of silica fume and cement type on the phenomenon of carbonation is also analyzed. Finally, it is presented a justification of results based on the existent database at LMABC-SET-EESC-USP.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2017-07-12
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.