Tesis Doctoral
DOI
10.11606/T.88.2011.tde-09062011-160804
Documento
Autor
Nombre completo
Lucinéia Ferreira Ceridorio
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2011
Director
Tribunal
Oliveira Junior, Osvaldo Novais de (Presidente)
Atvars, Teresa Dib Zambon
Neumann, Miguel Guillermo
Pezzin, Sérgio Henrique
Varanda, Laudemir Carlos
Título en portugués
Síntese de azopolímero e preparação de misturas para aplicações em optoeletrônicos
Palabras clave en portugués
Armazenamento óptico
Azopolímero
Langmuir e Langmuir-Blodgett filmes
Misturas
Resumen en portugués
Materiais poliméricos com propriedades de fotoisomerização, como os azopolímeros, apresentam grande potencial para aplicações em óptica não linear e dispositivos opto-eletrônicos. Entretanto há limitações para a aplicação dos azopolímeros devido à tendência à agregação dos cromóforos e dificuldade de formação de filmes. A mistura do azopolímero com polímeros metacrílicos e poli(3-alquiltiofenos) pode melhorar estas características sem acarretar prejuízos para a propriedade de isomerização fotoinduzida. Neste estudo o azopolímero foi sintetizado por ATRP usando o monômero DR1-MA, 4-[N-etil-N-(2-metacriloxietil)]-4- nitroazobenzeno, obtido a partir do corante Disperse Red 1 (DR1), os polímeros poli(metacrilato de hexila) (HPHex-MA) e poli(metacrilato de dodecila) (HPDod-MA) foram sintetizados por polimerização radicalar convencional a partir dos monômeros obtidos comercialmente e o poli(3-dodeciltiofeno) (HP3-DodT) obtido por polimerização oxidativa. As polimerizações foram bem sucedidas apresentando massas molares acima de 10.000 g/mol com polidispersividade relativamente baixa. As estruturas químicas foram confirmadas por espectroscopias UV-Vis, FTIR e RMN-H1. Misturas do azopolímero com os polímeros metacrílicos e o poli(3-alquiltiofeno) foram preparadas em diversas proporções e usadas na formação de filmes de Langmuir. Nestes filmes, isotermas de pressão de superfície apontaram interações para as três misturas em algumas proporções, entre elas a de 50%. Imagens de microscopia no ângulo de Brewster revelaram a contribuição do polímero metacrílico no espalhamento do filme do azopolímero sem a separação de fase. Os resultados de Espectroscopia de Infravermelho por Reflexão e Absorção com Polarização Modulada (PM-IRRAS) comprovaram que o comprimento da cadeia lateral do polímero afeta a organização molecular na interface. Filmes de Langmuir das misturas na proporção de 50% foram transferidos em substratos sólidos, obtendo os filmes Langmuir-Blodgett (LB). Comparações entre os filmes spin-coated e Langmuir-Blodgett mostraram que a organização molecular nos filmes nanoestruturados causa a redução na agregação de cromóforos e na hidrofobicidade da superfície. Filmes LB da mistura 50% HPDR1-MA/HPDod-MA com 101 camadas foram caracterizados quanto à capacidade de armazenamento óptico. Estes filmes apresentaram valores de birrefringência residual que permitem ser aplicados em armazenamento óptico com a vantagem de curtos tempos de escrita em comparação a outros filmes poliméricos.
Título en inglés
Synthesis of an azopolymer and preparation of blends for applications in optoelectronic
Palabras clave en inglés
Azopolymer
Langmuir and Langmuir-Blodgett films
Mixtures
Optical storage
Resumen en inglés
Polymeric materials with photoisomerization properties, such as the azopolymers, offer great potential for applications in non-linear optics and opto electronic devices. However, there are important limitations for the application of azopolymers, since azopolymers with high content of azobenzene moieties tend to aggregate and show poor film-formation properties. The combination of azopolymers with methacrylic polymers and poly (3-alkylthiophenes) can improve their properties without reducing the optical storage capability. In this study, the azopolymer poly[4-[[2-(methacryloyloxy)-ethyl]ethylamino]-4-nitroazobenzene], HPDR1-MA, was synthesized by Atom Transfer Radical Polymerization (ATRP), the poly (hexylmethacrylate) (HPHex-MA) and poly(dodecylmethacrylate)(HPDod-MA) were synthesized by conventional radical polymerization, the poly(3-dodecylthiophene) (HP3-DodT) via oxidative polymerization. The polymerizations were successful with molecular weights above 10.000 g/mol and relatively low polydispersities. The chemical structures were confirmed with UV-Vis, infrared and nuclear magnetic resonance spectroscopies. Mixtures of azopolymer with the methacrylic polymer and poly(3-alkylthiophenes) were prepared in various proportions and used in the formation of Langmuir films. In the latter, surface pressure isotherms indicated interactions between the film components, mainly for a proportion of 50% in weight of HPDR1-MA. Phase segregation was not apparent in the BAM images, which revealed that the methacrylic polymer improves the formation of the film Langmuir. Through PM-IRRAS, we noted that the length of the side chain of the polymer affects the molecular organization at the interface. Langmuir films of the mixtures in the proportion of 50% were transferred onto solid supports as Langmuir-Blodgett (LB ) films. Comparison of LB and spin-coated films demonstrated that the molecular organization of nanostructured films prevents the aggregation of chromophores and reduces the surface hydrophobicity. Optical Storage measurements were performed in 101-layer LB films of the mixture 50% HPDR1-MA/HPDod-MA. The photoinduced birefringence shows features that make these films useful for optical storage, with the advantage of short writing times in comparison to other azopolymer films.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-07-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.