Disertación de Maestría
DOI
10.11606/D.88.2007.tde-09042008-150513
Documento
Autor
Nombre completo
Henrique Nogueira Soares
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2007
Director
Tribunal
Tarpani, José Ricardo (Presidente)
Pereira, Luiz Edno
Spinelli, Dirceu
Título en portugués
Detecção por raios-x de trincas de fadiga em juntas rebitadas de Glare®
Palabras clave en portugués
Fadiga
Junta rebitada
Laminado metal fibra
Material aeronáutico
Radiografia de raios-x
Resumen en portugués
Foi realizado um estudo comparativo da capacidade de duas variantes do método de radiografia por raios- X em detectar trincas de fadiga em juntas sobrepostas rebitadas de laminado híbrido metal-fibra Glare® de uso aeronáutico. Durante os ensaios mecânicos de fadiga sob amplitude constante de tensão, diversos corpos de prova rebitados foram periodicamente inspecionados por raios-X, em ambas as modalidades convencional e digital. Raios-X em filmes convencionais digital. Raios-X em filmes convencionais proporcionaram ótimo detalhamento de trincas nas juntas mecânicas, enquanto que as imagens geradas pela modalidade digital apresentaram qualidade muito inferior, prejudicando ou até mesmo impedindo a avaliação do grau de integridade estrutural das juntas rebitadas.
Título en inglés
X-ray inspection of fatigue cracks in riveted lap joints of Glare&trade
Palabras clave en inglés
Airframe material
Fatigue
Ffiber metal-laminate
Riveted lap joint
X-ray radiography
Resumen en inglés
A comparison is performed on the ability of two modalities of nondestructive X-ray radiography method in detecting fatigue cracks in riveted lap joints of aeronautical grade fiber-metal laminate Glare™. During constant amplitude loading in fatigue testing riveted specimens were periodically inspected using both the conventional and digital X-ray methodology. Conventional film X-ray modality provided high quality images of growing cracks in the mechanical joints, whereas digital radiography generated faulty images, which impaired or even prevented the structural integrity assessment of the riveted joints.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
HenriqueSoares_M.pdf (20.93 Mbytes)
Fecha de Publicación
2008-04-10
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.