Disertación de Maestría
DOI
10.11606/D.88.2013.tde-06052013-192859
Documento
Autor
Nombre completo
André Diniz Rosa da Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2013
Director
Tribunal
Hernandes, Antonio Carlos (Presidente)
Mastelaro, Valmor Roberto
Vicente, Fabio Simões de
Título en portugués
Preparação e caracterização de um novo sistema vítreo multicomponente a base de óxido de boro
Palabras clave en portugués
Metais de transição
Vidros boratos
Vidros coloridos
Resumen en portugués
Vidros são materiais atraentes do ponto de vista científico e tecnológico, em especial porque algumas composições químicas permitem a fabricação em larga escala e/ou podem apresentar propriedades físico-químicas que os tornam candidatos promissores para aplicações como meio ativo para lasers, filtros ópticos, fibras ópticas, blindagens mecânicas ou como objeto de decoração ou utensílios domésticos ou como elemento para a construção civil, entre outras. Um dos desafios em preparar novas composições de materiais vítreos é garantir que não apareça o fenômeno da devitrificação. Este trabalho foi realizado com o objetivo de preparar e caracterizar uma nova matriz multicomponente, a base de óxido de boro, livre do fenômeno de cristalização. A matriz [50B2O3 - 15ZnO - 10PbO - 8MgO - 6K2O - 2Al2O3 - 2Nb2O5 - 5Si2O - 2Na2O] %wt pura e dopada com 0,1% mol de íons de metais de transição (MnO2, Fe2O3, CoO, NiO, CuO e CdCl2), foram preparadas em forno elétrico de atmosfera aberta usando cadinho de platina e caracterizadas usando as técnicas de: difração de raios X, análise térmica, densidade, pelo princípio de Arquimedes, microdureza Vickers, colorimetria, absorção óptica no intervalo ultravioleta-vísivel (UV-Vis) e transmissão óptica na região do infravermelho (FTIR). Resultados de difração de raios X confirmaram o caráter não cristalino das amostras vítreas. A adição de dopantes levou a mudança no número de coordenação na rede borato. Resultados de absorção óptica evidenciaram que a nova matriz desenvolvida com a adição de íons de metais de transição absorvem na região do visível e infravermelho próxima. Esses vidros tem potencial de aplicação na indústria de produtos decorativos e como filtros ópticos.
Título en inglés
Preparation and characterization of a new system base multicomponent glasses boron oxide
Palabras clave en inglés
Borate glass
Colored glasses
Transition metal
Resumen en inglés
Glasses are attractive materials on a scientific and technologic point of view especially because some of their chemical compositions can provide a large scale production and/or may present physicochemical properties that them become promising candidates for applications as laser active environments, optical filters, optical fibers, mechanical shielding, adornment, domestic tools or construction stuff, among others. One of the challenges in preparing new compositions of glassy materials is to ensure that does not appear the phenomenon of devitrification. This work was carried out in order to prepare and characterize a new multicomponent glassy matrix, the basis of boron oxide, free from crystallization phenomenon. Pure glassy samples of [50B2O3 - 15ZnO - 10PbO - 8MgO - 6K2O - 2Al2O3 - 2Nb2O5 - 5Si2O - 2Na2O % wt] and 0.1% mol of transition metal ions (MnO2, Fe2O3, CoO, NiO, CuO e CdCl2) doped were prepared in open atmosphere electric furnace using platinum crucible and characterized using x-ray diffraction, thermal analysis, density evaluation from Archimedes principle, Vickers microhardness measurements, colorimetry, UV-VIS optical absorption and IR optical transmission. X-ray diffraction results confirmed non-crystalline character of the vitreous samples. Dopants addition led to changing on the coordination number of the borate network. Optical absorption results showed that the new glassy matrix developed with addition of transition metal ions absorb in the visible and near infrared range. These glasses may have potential applications in decorative products and as optical filters.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-05-29
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.