Tesis Doctoral
DOI
10.11606/T.88.1999.tde-05122014-174109
Documento
Autor
Nombre completo
Paulo Antonio Martins Ferreira Ribeiro
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1999
Director
Tribunal
Giacometti, José Alberto (Presidente)
Leite, Edson Roberto
Nunes, Luiz Antonio de Oliveira
Santos, Maria Cristina dos
Zilio, Sérgio Carlos
Título en portugués
Caracterização dielétrica e eletroóptica do copolímero acrílico funcionalizado com o cromóforo 4-[N-etil-N-(2-hidroxietil)]amino-2-cloro-4-nitro-azobenzeno
Palabras clave en portugués
Acrylic copolymers
Dielectric characterization
Dyes
Electro-optic characterization
Resumen en portugués
Neste trabalho foi investigado o processo de relaxação em copolímeros metacrilicos funcionalizados com o grupo cromóforo 4-[N-etil-N-(2-hidroxietil)]amino-2'-cloro-4'nitro-azobenzeno (MMADRI3). Os copolímeros sintetizados foram caracterizados por espectrofotometria de visível e infravermelho, calorimetria diferencial de varredura, análise termogravimétrica e elipsometria. O triodo de corona foi utilizado para induzir a orientação dos cromóforos dipolares a temperaturas próximas da transição vítrea. Os valores do coeficiente eletroóptico linear r13 de filmes obtidos por derramento de solução podem alcançar 14 pm/V em amostras funcionalizadas com 43%de cromóforo.O efeito piezoelétricoé significativo para amostras contendo 4% de cromóforo sendo a sua origem atribuída à carga espacial. A relaxação orientacional dos cromóforos foi estudada medindo-se o decaimento do coeficiente eletroóptico e a relaxação dielétrica a diferentes temperaturas. O processo de relaxação foi interpretado utilizando a equação de Kohlraush-Williams-Watts (KWW) aplicada aos domínios do tempo e da freqüência. O tempo de relaxação característico τ e o parâmetro b da equação de KWW foram obtidos como função da temperatura desde a temperatura ambiente até acima da temperatura de transição vítrea. O parâmetro b à temperatura de transição vítrea aproxima-se de 0,6 valor que é atribuído a forças de curto alcance. As medidas dielétricas revelaram duas bandas de relaxação β e α respectivamente a baixas e a altas temperaturas. A relaxação a está relacionada com a transição vítrea e à desorientação dos cromóforos. A dependência de τ foi fundamentada nas equações de Arrhenius e de Vogel-Fulcher-Tarmnann-Hesse (VFTH), respectivamente a baixas e a altas temperaturas. Os parâmetros de VFTH encontram-se próximos dos considerados universais. O comportamento de τ em toda a gama de temperaturas, foi explicado pela equação de Adam-Gibbs, usando-se os parâmetros de VFTH. O resfriamento a taxas lentas após o processo de polarização aumenta substancialmente o tempo de relaxação e a sua energia de ativação. Os expoentes m e n do modelo de Dissado-Hill baseado na interação de multicorpos foram obtidos em função da temperatura. Os valores do parâmetro n ficam dentro do esperado pela teoria
Título en inglés
Dielectric and electro-optic characterization of the acrylic copolymer containing 4-[N-etyl-N-(2-hydroxietil)]amie-2-cloro-4-nitro-azobenzene group
Palabras clave en inglés
Caracterização dielétrica
Caraterização eletro-óptica
Copolímero acrílico
Corantes
Resumen en inglés
The relaxation process of side-chain methacrylate copolymers functionalized with the nonlinear optical azo chromophore 4-[Nethyl-N-(2-hydroxyethyl)]-amino-2'-chloro-4-nitroazobenzene (MMADR13) was investigated. The copolymers synthesized were characterized by visible and infrared spectrophotometry, differential scanning calorimetry, thermogravimetric analysis and ellipsometry. The corona triode was employed to induce the orientation of the dipolar chromophore at a temperature near the glass transition. The linear eletrooptic coefficient r13 of cast fllms can reach values as high as 14 pm/V in samples with 43% of chromophore contento The piezoeletric effect attributed to space charge was only significant in the lowest chromophore content samples (4%). Electrostriction was shown to affect to some extent the quadratic electrooptic measurements. The chromophore relaxation at different temperatures was investigated by both electrooptic decay and dielectric measurements. The relaxation process was interpreted using the Kohlraush-Williams-Watts (KWW) equation both in the time and frequency domains. From the KWW equation the characteristic relaxation time τ and the stretching parameter b were obtained from room temperature to temperatures above the glass transition. Near the glass transition b is ca 0.6 which is characteristic of short range interactions. Dielectric measurements revealed two relaxation bands, β and α, at low and high temperatures, respectively. The α relaxation was attributed to the glass transition and to the 10ss of chromophore orientational order. The temperature behavior of τ was interpreted by the Arrhenius and Vogel-Fulcher-Tammann-Hesse (VFTH) equations. at low and high temperatures. respectivelly. The VFTH parameters lie close to the so-called universal values. In addition the overall temperature dependence was explained by the Adam-Gibbs equation using the VFTH parameters. Using a small cooling rate after corona poling increases substantially the relaxation time and the activation energy .The power law exponents m and n. from Dissado-Hill manybody interactions model were obtained as a function of temperature. The n values are in the range of expected values for the many-body interactions model
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-01-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.