Mémoire de Maîtrise
DOI
10.11606/D.88.2009.tde-04062009-145511
Document
Auteur
Nom complet
Aristides Rodrigues Mattar Junior
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2009
Directeur
Jury
Casteletti, Luiz Carlos (Président)
Canale, Lauralice de Campos Franceschini
Soufen, Carlos Alberto
Titre en portugais
Influência dos elementos de liga Cu-Ni-Mo nas propriedades mecânicas e na austemperabilidade do ADI
Mots-clés en portugais
Ferro fundido nodular austemperado (ADI). Austêmpera. Austemperabilidade. Ausferrita. Propriedades m
Resumé en portugais
O ADI constitui-se no desenvolvimento mais recente na família dos ferros fundidos nodulares. Com o tratamento de austêmpera, consegue-se produzir uma microestrutura única, constituída de ferrita acicular e austenita estável rica em carbono, a ausferrita, proporcionando alta resistência mecânica aliada à ductilidade e tenacidade, além de boa resistência à fadiga e ao desgaste. Neste trabalho estudou-se o efeito dos elementos de liga Cu, Ni e Mo nas propriedades mecânicas e austemperabilidade do ADI. Foram produzidas barras cilíndricas de ferros fundidos nodulares nos diâmetros de Ø2, Ø3 e Ø4 ligadas com Cu, Cu-Ni, Cu-Ni- Mo respectivamente. Os corpos de prova utilizados nos ensaios de tração, impacto e microdesgaste foram retirados a meio-raio das barras. Posteriormente, cada conjunto de corpo de prova foi austenitizado a 890°C durante 2 horas, sendo em seguida submetido a uma condição de tratamento de austêmpera específica, combinando temperaturas de austêmpera de 300 e 360°C e tempos de 1, 2, 3 e 4 horas. Realizou-se análises microestruturais ópticas e por microscopia eletrônica de varredura para correlacionar propriedades mecânicas com a microestrutura. Na análise de austemperabilidade, as barras cilíndricas foram austemperadas para verificar a variação de microestrutura em função do raio da barra. Verificou-se que a temperatura de austêmpera exerce forte influência na microestrutura do ADI e consequentemente nas propriedades de tração, ductilidade, tenacidade e resistência ao desgaste. Nos tratamentos a 300°C obteve-se uma microestrutura mais refinada, com maior quantidade de ferrita acicular, responsável pela maior resistência mecânica e resistência ao desgaste; enquanto que no tratamento realizado a 360°C obteve-se uma microestrutura mais grosseira, com maior quantidade de austenita estável, responsável pela melhor ductilidade e tenacidade. Nos tempos de austêmpera analisados, não ocorreram variações significativas nas microestruturas e propriedades mecânicas. A resistência mecânica e a tenacidade decresceram com a adição de Mo, provavelmente devido à segregação deste elemento, mas a resistência ao desgaste a seco e a austemperabilidade foram mais efetivas em comparação com ligas contendo Cu e Cu-Ni. No ensaio de desgaste usando-se lubrificante, o ADI ligado com Cu-Ni austemperado a 360°C apresentou uma resistência ao desgaste um pouco inferior a de um aço 17CrNiMo6 cementado.
Titre en anglais
Influence of alloys elements Cu-Ni-Mo on mechanical properties and austemperability of ADI.
Mots-clés en anglais
Alloy elements.
Ausferrite
Austemperability
Austempered Ductile Iron (ADI)
Austempering
Mechanical Properties
Wear Resistance
Resumé en anglais
The ADI is the most recent development in the nodular iron family. With the austempering treatment, a unique microstructure, consisting of acicular bainite ferrite and stable austenite rich in carbon, named ausferrite is produced. This microstructure provides high mechanical strength combined with ductility, toughness and good fatigue and wear resistances. In this work, the effect of alloying elements Cu, Ni and Mo on the mechanical properties and austemperability of the ADI were studied. To conduct these studies, cylindrical bars with diameters of Ø2", Ø3" and Ø4" were cast with Cu, Cu-Ni and Cu-Ni-Mo alloying, respectively. The samples were then manufactured by removing specimens from the bar midradius position. Subsequently, each set of the samples was austenitized at 890°C for 2 hours, and then subjected different conditions of austempering treatment. These treatments were developed by combining austempering temperatures of 300 and 360°C with austempering times of 1, 2, 3 and 4 hours. Microstructural analysis was carried out using optical and scanning electron microscopy to correlate mechanical properties with the microstructure. In the austemperability analysis, cylindrical bars were austempered (at 360°C for 3 hours) to correlate microstructure and radius. The experimental results showed that the austempering temperature exerts strong influence on the ADI´s microstructure and consequently on the mechanical properties. The austempering temperature of 300°C produced the best results, a refined microstructure, with a greater amount of acicular ferrite, responsible for greater strength and wear resistance. The austempering temperature of 360°C produced a coarse microstructure, with larger amount of austenite and responsible for better ductility and toughness. The austempering times used in this work did not produce significant variations in the properties and microstructures. Regarding alloying elements, the mechanical strength and toughness decreased with the addition of Mo, probably due to the segregation of this element, but the wear resistance and austemperability were more effective when compared with the alloys containing Cu and Cu-Ni. In the lubricated wear test, the ADI alloyed with Cu-Ni and austempered at 360°C presented a wear resistance only a fraction lower than a cemented 17CrNiMo6 steel.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2009-08-07
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.