Disertación de Maestría
DOI
10.11606/D.88.2003.tde-01122014-113352
Documento
Autor
Nombre completo
Marcia Yumi Teruya
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2003
Director
Tribunal
Alves, Neri (Presidente)
Bianchi, Rodrigo Fernando
Pessan, Luiz Antonio
Título en portugués
Blendas condutoras elétricas obtidas a partir do látex de seringueira Hevea Brasiliensis com polianilina
Palabras clave en portugués
Borracha natural
Condutividade elétrica.
Nanocamadas
Polianilina
Resumen en portugués
É grande o interesse em combinar as propriedades mecânicas e elétricas de diferentes materiais poliméricos. Neste trabalho, filmes de Borracha Natural com camadas superficiais condutoras de polianilina (PANI) são preparados e caracterizados por diferentes técnicas. A PANI dopada foi depositada em ambos os lados do filme de borracha por polimerização química "in situ" da anilina a temperatura ambiente. O processo da polimerização da PANI "in situ" foi otimizado variando a concentração dos reagentes químicos com o objetivo de se obter uma camada de PANI com espessura desejada, boa adesão na borracha e que produzisse também aumento da condutividade elétrica na superfície. As amostras obtidas são caracterizadas usando-se Microscopia Eletrônica de Varredura, Microscopia Óptica, Difratometria de raios-X, análise por Calorimetria Diferencial de Varredura, análise Termo-Dinâmico-Mecânica, análise Termogravimétrica, Espectroscopia no FT-IR, Ensaio Mecânico e condutividade elétrica na superfície e no volume dos filmes preparados. Os resultados mostram que os filmes produzidos são do tipo multicamadas, pois não há uma interpenetração da PANI na borracha. A melhor condutividade e uniformidade é obtida com filmes preparados com três deposições, atingindo a ordem de 10-7 S/cm
Título en inglés
Electrical conductive blends obtained using the rubber tree Hevea brasiliensis latex with polyaniline
Palabras clave en inglés
Electrical conductive
Nanolayers
Natural rubber
Polyaniline
Resumen en inglés
The combination of properties of different polymeric materials in one sample is of great interest. In this work natural rubber films covered with a layer of conductive polyaniline (PANI) were prepared and studied by means of several experimental techniques. The doped PANI layer was deposited onto both rubber films surfaces by the "in situ" polymerization technique. The polymerization of PANI was performed at room temperature and the deposition process was optimized in order to obtain a PANI layer with an adequate thickness, good adhesion to the rubber and to promote the increase of its surface electric conductivity. Samples were characterized employing the scanning electron microscopy, optical microscopy, X-ray diffractometry, differential scanning calorimetry, thermo gravimetric analysis, dynamic mechanical thermal analysis, mechanical analysis and surface/volume electric conductivity. Results showed that the formed films consisted of a PANI layer that did not penetrated in the rubber. The better uniformity of deposition and maximum electric conductivity of the order of 10-7 S/cm was obtained on films that were prepared by deposition of three PANl layers
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
MarciaYumiTeruyaM.pdf (15.63 Mbytes)
Fecha de Publicación
2014-12-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.