Mémoire de Maîtrise
DOI
10.11606/D.85.2008.tde-31082009-133513
Document
Auteur
Nom complet
Graziela Cristiane Telles da Silva
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2008
Directeur
Jury
Muccillo, Eliana Navarro dos Santos (Président)
Martinelli, José Roberto
Rey, José Fernando Queiruga
Titre en portugais
Efeito da adição de óxido de cobalto na sinterização e na condutividade elétrica da zircônia estabilizada com ítria
Mots-clés en portugais
aditivos cerâmicos
dondutividade elétrica
sinterização
Zircônia
Resumé en portugais
A zircônia estabilizada com ítria é um material com diversas aplicações tecnológicas. Uma de suas aplicações é como eletrólito sólido em células a combustível de óxido sólido. Os pós de zircônia estabilizada com ítria disponíveis comercialmente densificam a temperaturas superiores a 1400 ºC. Redução na temperatura de sinterização da zircônia seria muito útil, pois permitiria a realização da sinterização simultânea (co-firing) do eletrólito sólido e do anodo, implicando em redução de custo do processo na fabricação de células a combustível. Neste trabalho, os efeitos produzidos do Co na densificação da 8YSZ, principalmente em baixos teores do aditivo, foi estudado, como também a condutividade elétrica da zircônia-estabilizada com ítria, visando determinar o efeito da adição de Co. Foram preparados compactos com carbonato de cobalto e 8YSZ comercial em composições 8YSZ + x% mol Co com x = 0; 0,025; 0,05; 0,1; 0,25; 0,5; 1; 2; 3; 4; 5; 7,5 e 10, por prensagem seguida de sinterização ao ar em diversas temperaturas e tempo de patamar. Os compactos sinterizados foram caracterizados por diversas técnicas. A espectroscopia Raman e a difração de raios X permitiram identificar o Co3O4 como fase predominante após a sinterização, quando o aditivo excede o limite de solubilidade. A densidade sinterizada aumentou com a adição de pequenos teores de Co, mas não foi suficiente para reduzir a temperatura de sinterização abaixo de 1400 ºC. O tamanho médio de grãos aumentou com a temperatura de sinterização. A condutividade elétrica diminui com a adição de Co para teores ³ 1% mol, mas apresenta pequeno aumento para teores de 0,025% mol.
Titre en anglais
Effect of Cobalt Oxide on Sintering and Electrical Conductivity of Yttria Stabilized Zirconia
Mots-clés en anglais
additives.
electrical conductivity
sintering
zirconia
Resumé en anglais
Yttria stabilized zirconia has a wide range of applications including electrochemical devices, oxygen sensors and permeable membranes. Yttria stabilized zirconia is the preferred solid electrolyte in current solid oxide fuel cells. Commercially available yttria stabilized zirconia powders are usually sintered at temperatures higher than 1400 ºC. Reduction of the sintering temperature is desirable to allow for co-firing the solid electrolyte and the anode materials, thereby reducing the fabrication cost. In this work, the effects produced by small amounts of Co addition on sintering and on electrical conductivity of 8YSZ were investigated. Green compacts were prepared by uniaxial pressing mixtures of 8YSZ + x mol% Co with x = 0; 0.025; 0.05; 0.1; 0.25; 0.5; 1; 2; 3; 4; 5; 7.5 and 10 followed by sintering at different dwell temperatures and soaking times. Several techniques were used to characterize the sintered compacts. Results of Raman spectroscopy along with those of Xray diffraction allowed for the identification of the cobalt oxide formed (Co3O4) when the solubility limit is exceeded. The sintered density increased with small Co additions. However, the sintering temperature is still around 1400 ºC. The average grain size increased with Co addition and with increase of the sintering temperature. The electrical conductivity remains almost unchanged with Co additions up to ~ 0.5 mol% and decreases for higher additive contents. However, a small increase of the electrical conductivity occurs at 0.025 mol% Co.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2009-09-23
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.