Disertación de Maestría
DOI
10.11606/D.85.2008.tde-31082009-133513
Documento
Autor
Nombre completo
Graziela Cristiane Telles da Silva
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Muccillo, Eliana Navarro dos Santos (Presidente)
Martinelli, José Roberto
Rey, José Fernando Queiruga
Título en portugués
Efeito da adição de óxido de cobalto na sinterização e na condutividade elétrica da zircônia estabilizada com ítria
Palabras clave en portugués
aditivos cerâmicos
dondutividade elétrica
sinterização
Zircônia
Resumen en portugués
A zircônia estabilizada com ítria é um material com diversas aplicações tecnológicas. Uma de suas aplicações é como eletrólito sólido em células a combustível de óxido sólido. Os pós de zircônia estabilizada com ítria disponíveis comercialmente densificam a temperaturas superiores a 1400 ºC. Redução na temperatura de sinterização da zircônia seria muito útil, pois permitiria a realização da sinterização simultânea (co-firing) do eletrólito sólido e do anodo, implicando em redução de custo do processo na fabricação de células a combustível. Neste trabalho, os efeitos produzidos do Co na densificação da 8YSZ, principalmente em baixos teores do aditivo, foi estudado, como também a condutividade elétrica da zircônia-estabilizada com ítria, visando determinar o efeito da adição de Co. Foram preparados compactos com carbonato de cobalto e 8YSZ comercial em composições 8YSZ + x% mol Co com x = 0; 0,025; 0,05; 0,1; 0,25; 0,5; 1; 2; 3; 4; 5; 7,5 e 10, por prensagem seguida de sinterização ao ar em diversas temperaturas e tempo de patamar. Os compactos sinterizados foram caracterizados por diversas técnicas. A espectroscopia Raman e a difração de raios X permitiram identificar o Co3O4 como fase predominante após a sinterização, quando o aditivo excede o limite de solubilidade. A densidade sinterizada aumentou com a adição de pequenos teores de Co, mas não foi suficiente para reduzir a temperatura de sinterização abaixo de 1400 ºC. O tamanho médio de grãos aumentou com a temperatura de sinterização. A condutividade elétrica diminui com a adição de Co para teores ³ 1% mol, mas apresenta pequeno aumento para teores de 0,025% mol.
Título en inglés
Effect of Cobalt Oxide on Sintering and Electrical Conductivity of Yttria Stabilized Zirconia
Palabras clave en inglés
additives.
electrical conductivity
sintering
zirconia
Resumen en inglés
Yttria stabilized zirconia has a wide range of applications including electrochemical devices, oxygen sensors and permeable membranes. Yttria stabilized zirconia is the preferred solid electrolyte in current solid oxide fuel cells. Commercially available yttria stabilized zirconia powders are usually sintered at temperatures higher than 1400 ºC. Reduction of the sintering temperature is desirable to allow for co-firing the solid electrolyte and the anode materials, thereby reducing the fabrication cost. In this work, the effects produced by small amounts of Co addition on sintering and on electrical conductivity of 8YSZ were investigated. Green compacts were prepared by uniaxial pressing mixtures of 8YSZ + x mol% Co with x = 0; 0.025; 0.05; 0.1; 0.25; 0.5; 1; 2; 3; 4; 5; 7.5 and 10 followed by sintering at different dwell temperatures and soaking times. Several techniques were used to characterize the sintered compacts. Results of Raman spectroscopy along with those of Xray diffraction allowed for the identification of the cobalt oxide formed (Co3O4) when the solubility limit is exceeded. The sintered density increased with small Co additions. However, the sintering temperature is still around 1400 ºC. The average grain size increased with Co addition and with increase of the sintering temperature. The electrical conductivity remains almost unchanged with Co additions up to ~ 0.5 mol% and decreases for higher additive contents. However, a small increase of the electrical conductivity occurs at 0.025 mol% Co.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-09-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.